| SABIC® PP 505P is a multi purpose grade for extrusion and injection moulding applications. SABIC® PP 505P provides an excellent stretch ability and is suitable for extrusion of tapes, strapping, high tenacity yarns but also for thermoformed articles. For injection moulded parts SABIC® PP 505P shows a moderate stiffness, good impact resistance and very good surface hardness. SABIC PP505P is suitable for production of caps and closures and house ware articles. SABIC® PP 505P is a low mfi grade typically used in extrusion applications like sheet and thermoforming. SABIC® PP 505P is typically used in dairy, flower pots, yellow fats and disposables plates and cups. However, customers use this grade also in combination with fillers like Talc and CaCO3.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | High impact resistance,Wide molecular weight distribution,Good Hardness,Homopolymer |
| Availabilitys | Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 2.0 | g/10min | ASTM D1238，ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 1% secant | 1500 | MPa | ASTM D638 |
| — | 1500 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| yield | 36.0 | MPa | ASTM D638 |
| yield | 37.0 | MPa | ISO 527-2/1A/50 |
| Tensile strain | |||
| yield | 10 | % | ASTM D638 |
| yield | 10 | % | ISO 527-2/1A/50 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 4.5 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃ | 40 | J/m | ASTM D256-A |
| 23℃ | 3.5 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 90.0 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 85.0 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed | 60.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 55.0 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| — | 152 | ℃ | ASTM D1525, ISO 306/A 6 6 |
| — | 88.0 | ℃ | ASTM D1525, ISO 306/B 7 7 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.039 in/min |
| 3. 2.0 in/min |
| 4. testbar 80*10*4mm |
| 5. Rate B (120°C/h), Loading 1 (10 N) |
| 6. Rate B (120°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |