SABIC® PP 526K

About
SABIC® PP 526K is a grade developed for efficient thermoforming. SABIC® PP 526K is formulated with a combined processing, antistatic and nucleator package of the next generation. The nucleator technology provides higher stiffness and good transparency/gloss in the thermoformed part. The fact that the polymer/additive package gives higher isotropic processing behaviour reduces warpage, ovality and other dimensional problems. Application: SABIC® PP 526K is typically used for various thermoformed parts sensitive to dimensional stability. Customers use this grade as natural or coloured, ranging from food containers to disposables, yellow fats and lids. This product is not intended for and must not be used in any pharmaceutical/medical applications.&&

About

SABIC® PP 526K is a grade developed for efficient thermoforming. SABIC® PP 526K is formulated with a combined processing, antistatic and nucleator package of the next generation. The nucleator technology provides higher stiffness and good transparency/gloss in the thermoformed part. The fact that the polymer/additive package gives higher isotropic processing behaviour reduces warpage, ovality and other dimensional problems. Application: SABIC® PP 526K is typically used for various thermoformed parts sensitive to dimensional stability. Customers use this grade as natural or coloured, ranging from food containers to disposables, yellow fats and lids. This product is not intended for and must not be used in any pharmaceutical/medical applications.&&

Product Description
Supplier	SABIC
Generic	PP homopolymerization
Material Status	Commercial: Active
Features	Excellent Processability,Good Dimensional Stability,Wide molecular weight distribution,Nucleation,Antistatic property,High isotacticity,Homopolymer
Availabilitys	Europe
Process Methods	Thermo forming

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.905	g/cm³	ASTM D792, ISO 1183
Melt Flow Rate
230℃，2.16kg	3.0	g/10min	ASTM D1238，ISO 1133

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus
1% secant	2150	MPa	ASTM D638
—	2050	MPa	ISO 527-2/1A/1
tensile strength
yield	40.0	MPa	ASTM D638
yield	40.0	MPa	ISO 527-2/1A/50
Tensile strain
yield	7.0	%	ASTM D638
yield	6.0	%	ISO 527-2/1A/50

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
23℃	4.5	kJ/m²	ISO 179/1eA
Impact strength of cantilever beam notch
23℃	35	J/m	ASTM D256-A
23℃	3.0	kJ/m²	ISO 180-1A

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	120	℃	ASTM D648
0.45 MPa, unannealed	115	℃	ISO 75-2/Bf
1.8 MPa, unannealed	70.0	℃	ASTM D648
1.8 MPa, unannealed	65.0	℃	ISO 75-2/Af
Vicat Softening Temp
—	155	℃	ASTM D1525，ISO 306/A120 6 6
B120	100	℃	ASTM D1525, ISO 306/B120 7 7

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.