| About |
|---|
| This grade combines an excellent stiffness with high impact resistance. It has a narrow molecular weight distribution and a low tendency to warp. Excellent flow in combination with high crystallisation speed enables outstanding processability aiming at easy mould filling and short cycle times. Due to the mentioned performance this grade is suitable for usage in several kinds of containers. The excellent high gloss level makes this material also favourable for household applications. This product is not intended for and must not be used in any pharmaceutical/medical applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Low warping,Excellent Processability,Good surface appearance,High impact resistance,Good liquidity,Nucleation,Quick molding cycle,Block Copolymer,Weight distribution |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.905 | g/cm³ | ASTM D792 , ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 15 | g/10min | ASTM D1238，ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20℃ | 6.0 | kJ/m² | ISO 179/1eA |
| 0℃ | 8.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 13 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| -20℃ | 65 | J/m | ASTM D256-A |
| 0℃ | 75 | J/m | ASTM D256-A |
| 23℃ | 100 | J/m | ASTM D256-A |
| -20℃ | 6.0 | kJ/m² | ISO 180-1A |
| 0℃ | 7.0 | kJ/m² | ISO 180-1A |
| 23℃ | 11 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 105 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 100 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed | 65.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 60.0 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| — | 151 | ℃ | ASTM D1525 6 , ISO 306/A120 6 |
| B120 | 80.0 | ℃ | ASTM D1525 7 , ISO 306/B120 7 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 65 | ISO 868 | |
| Rockwell hardness | |||
| R-level | 97 | ASTM D785 | |
| Tensile modulus | |||
| 1% secant | 1600 | MPa | ASTM D638 |
| — | 1550 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| yield | 26.0 | MPa | ASTM D638 |
| yield | 27.0 | MPa | ISO 527-2/1A/50 |
| Tensile strain | |||
| yield | 4.0 | % | ASTM D638 |
| yield | 4.0 | % | ISO 527-2/1A/50 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. 2.0 in/min |
| 4. testbar 80*10*4mm |
| 5. Rate B (120°C/h), Loading 1 (10 N) |
| 6. Rate B (120°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |