SABIC® PP PCGH10

About
SABIC® PP PCGH10 SABIC® PP grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity. SABIC® PP PCGH10 is designed with well balanced mechanical properties and easy processing behaviour for injection moulding of healthcare applications such as caps and closures, 3-part syringes, both also suitable for extrusion of film, both mono layer films and co extruded films as well. This grade offers a high stifness combined with excellent flow properties. Due to its narrow molecular weight distribution it is very suitable for thin walled, warpage critical applications. Compliance to regulations: SABIC®PP PCGH10 complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI). The product mentioned herein may not be used for medical healthcare devices or materials intended for temporary or permanent implementation in the human body.&&SABIC® PP PCGH10 PP Homopolymer for Healthcare SABIC® PP grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity. SABIC® PP PCGH10 is typically designed for healthcare applications, such as caps and closures, parts for medical devices and medical film. This grade offers a high stifness with moderate impact strength. Compliance to regulations: SABIC®PP PCGH10 complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI). The product mentioned herein may not be used for medical healthcare devices or materials intended for temporary or permanent implementation in the human body.&&

About

SABIC® PP PCGH10 SABIC® PP grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity. SABIC® PP PCGH10 is designed with well balanced mechanical properties and easy processing behaviour for injection moulding of healthcare applications such as caps and closures, 3-part syringes, both also suitable for extrusion of film, both mono layer films and co extruded films as well. This grade offers a high stifness combined with excellent flow properties. Due to its narrow molecular weight distribution it is very suitable for thin walled, warpage critical applications. Compliance to regulations: SABIC®PP PCGH10 complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI). The product mentioned herein may not be used for medical healthcare devices or materials intended for temporary or permanent implementation in the human body.&&SABIC® PP PCGH10 PP Homopolymer for Healthcare SABIC® PP grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity. SABIC® PP PCGH10 is typically designed for healthcare applications, such as caps and closures, parts for medical devices and medical film. This grade offers a high stifness with moderate impact strength. Compliance to regulations: SABIC®PP PCGH10 complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI). The product mentioned herein may not be used for medical healthcare devices or materials intended for temporary or permanent implementation in the human body.&&

Product Description
Supplier	SABIC
Generic	PP homopolymerization
Material Status	Commercial: Active
Features	Good Rigidity,High purity,High elastic,Good liquidity,Weight distribution,Homopolymer
Availabilitys	North America,Latin America,Europe
Process Methods	Film extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.905	g/cm³	ASTM D792, ISO 1183
Melt Flow Rate
230℃，2.16kg	11	g/10min	ASTM D1238，ISO 1133

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
23℃	4.0	kJ/m²	ISO 179/1eA
Impact strength of cantilever beam notch
23℃	25	J/m	ASTM D256-A
23℃	3.0	kJ/m²	ISO 180-1A

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	95.0	℃	ASTM D648
0.45 MPa, unannealed	90.0	℃	ISO 75-2/Bf
1.8 MPa, unannealed	60.0	℃	ASTM D648
1.8 MPa, unannealed	55.0	℃	ISO 75-2/Af
Vicat Softening Temp
—	154	℃	ASTM D1525，ISO 306/A120 5 6
B120	95.0	℃	ASTM D1525, ISO 306/B120 6 7

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	69		ISO 868
Rockwell hardness
R-level	111		ASTM D785
Tensile modulus
1% secant	1800	MPa	ASTM D638
—	1700	MPa	ISO 527-2/1A/1
tensile strength
yield	36.0	MPa	ASTM D638
yield	36.0	MPa	ISO 527-2/1A/50
Tensile strain
yield	9.0	%	ASTM D638
yield	9.0	%	ISO 527-2/1A/50

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.