SABIC® PP PCGH19

About
SABIC® PP PCGH19 SABIC® PP grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity. SABIC® PP PCGH19 is typically designed for injection molding of healthcare such as caps and closures, 3-part syringes and other thin walled applications. This grade offers a high stifness combined with excellent flow properties. Due to its narrow molecular weight distribution it is very suitable for thin walled, warpage critical applications. SABIC® PP PCGH19 complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI). The product mentioned herein may not be used for medical healthcare devices or materials intended for temporary or permanent implementation in the human body.&&SABIC® PP PCGH19 PP Homopolymer for Healthcare SABIC® PP grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity. SABIC® PP PCGH19 is typically designed for injection molding of healthcare applications such as caps and closures, 3-part syringes and other thin walled parts. This grade offers a high stiffness combined with excellent flow properties. Due to its narrow molecular weight distribution it is very suitable for thin walled, warpage critical applications. Compliance to regulations: SABIC® PP PCGH19 complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI). The product mentioned herein may not be used for medical healthcare devices or materials intended for temporary or permanent implementation in the human body.&&

About

SABIC® PP PCGH19 SABIC® PP grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity. SABIC® PP PCGH19 is typically designed for injection molding of healthcare such as caps and closures, 3-part syringes and other thin walled applications. This grade offers a high stifness combined with excellent flow properties. Due to its narrow molecular weight distribution it is very suitable for thin walled, warpage critical applications. SABIC® PP PCGH19 complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI). The product mentioned herein may not be used for medical healthcare devices or materials intended for temporary or permanent implementation in the human body.&&SABIC® PP PCGH19 PP Homopolymer for Healthcare SABIC® PP grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity. SABIC® PP PCGH19 is typically designed for injection molding of healthcare applications such as caps and closures, 3-part syringes and other thin walled parts. This grade offers a high stiffness combined with excellent flow properties. Due to its narrow molecular weight distribution it is very suitable for thin walled, warpage critical applications. Compliance to regulations: SABIC® PP PCGH19 complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI). The product mentioned herein may not be used for medical healthcare devices or materials intended for temporary or permanent implementation in the human body.&&

Product Description
Supplier	SABIC
Generic	PP homopolymerization
Material Status	Commercial: Active
Features	Good Rigidity,Low warping,High purity,High liquidity,High elastic,Weight distribution,Homopolymer
Availabilitys	North America,Latin America,Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.905	g/cm³	ASTM D792, ISO 1183
Melt Flow Rate
230℃，2.16kg	19	g/10min	ASTM D1238，ISO 1133

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
23℃	4.0	kJ/m²	ISO 179/1eA
Impact strength of cantilever beam notch
23℃	25	J/m	ASTM D256-A
23℃	3.0	kJ/m²	ISO 180-1A

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	95.0	℃	ASTM D648
0.45 MPa, unannealed	90.0	℃	ISO 75-2/Bf
1.8 MPa, unannealed	65.0	℃	ASTM D648
1.8 MPa, unannealed	60.0	℃	ISO 75-2/Af
Vicat Softening Temp
—	152	℃	ASTM D1525，ISO 306/A120 5 6
B120	94.0	℃	ASTM D1525, ISO 306/B120 6 7

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	71		ISO 868
Rockwell hardness
R-level	112		ASTM D785
Tensile modulus
1% secant	1850	MPa	ASTM D638
—	1800	MPa	ISO 527-2/1A/1
tensile strength
yield	37.0	MPa	ASTM D638
yield	37.0	MPa	ISO 527-2/1A/50
Tensile strain
yield	9.0	%	ASTM D638
yield	9.0	%	ISO 527-2/1A/50

Notes
1. Typical properties: these are not to be construed as specifications.
2. 0.039 in/min
3. 2.0 in/min
4. testbar 80104mm
5. Rate B (120°C/h), Loading 1 (10 N)
6. Rate B (120°C/h), Loading 2 (50 N)
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.