| About |
|---|
| This grade combines very high impact resistance, also at low temperatures, with a good stiffness and offers very good flow properties. Due to its narrow molecular weight distribution and very low tendency to warp, it is highly suitable for injection moulding of crates & boxes, suitcase shells and automotive parts. This grade is UV-stabilised and also available in a general purpose additive package. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Weather resistance is good,Low warping,High impact resistance,Good liquidity,Block Copolymer,Weight distribution,low-temperature impact resistance |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 14 | g/10min | ASTM D1238，ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20℃ | 8.0 | kJ/m² | |
| 0℃ | 15 | kJ/m² | |
| 23℃ | 60 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| 23℃ | 无断裂 | ISO 179/1eU | |
| Impact strength of cantilever beam notch | |||
| -20℃ | 100 | J/m | ASTM D256-A |
| 0℃ | 180 | J/m | ASTM D256-A |
| 23℃ | 无断裂 | ASTM D256-A，ISO 180-1A | |
| -20℃ | 9.0 | kJ/m² | ISO 180-1A |
| 0℃ | 13 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 85.0 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 80.0 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed | 55.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 50.0 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| — | 145 | ℃ | ASTM D1525，ISO 306/A120 6 6 |
| B120 | 65.0 | ℃ | ASTM D1525, ISO 306/B120 7 7 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 60 | ISO 868 | |
| Rockwell hardness | |||
| R-level | 85 | ASTM D785 | |
| Tensile modulus | |||
| 1% secant | 1050 | MPa | ASTM D638 |
| — | 1000 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| yield | 21.0 | MPa | ASTM D638 |
| yield | 21.0 | MPa | ISO 527-2/1A/50 |
| Tensile strain | |||
| yield | 6.0 | % | ASTM D638 |
| yield | 6.0 | % | ISO 527-2/1A/50 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. 2.0 in/min |
| 4. testbar 80*10*4mm |
| 5. Rate B (120°C/h), Loading 1 (10 N) |
| 6. Rate B (120°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |