| About |
|---|
| SABIC® PPcompound 3020B is a 20% talc-filled Polypropylene. The material’s high modulus and it’s thermal and UV stabilization makes it suitable for exterior applications, like cowl top panels. SABIC® PPcompound 3020B is a designated automotive grade.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Heat Stabilized |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 12 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| 24 hrs | 1.1 | % | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23 ℃, injection molding | 4.4 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ISO 180/4A | ||
| -20 ℃, injection molding | 2.2 | kJ/m² | ISO 180-4A |
| 0 ℃, injection molding | 2.7 | kJ/m² | ISO 180-4A |
| 23 ℃, injection molding | 3.1 | kJ/m² | ISO 180-4A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 120 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | 150 | ℃ | ISO 306/A |
| Linear coefficient of thermal expansion | |||
| MD | ASTM D696 | ||
| -30 to 30 ℃ | 5.0E-5 | cm/cm/℃ | ASTM D696 |
| 23 to 80 ℃ | 1.0E-4 | cm/cm/℃ | ASTM D696 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, injection molding | 72 | ISO 868 | |
| tensile strength | ISO 527-2/5/50 | ||
| Yield, 3.20 mm, injection molding | 29.0 | MPa | ISO 527-2/5/50 |
| Fracture, 3.20 mm, injection molded | 27.0 | MPa | ISO 527-2/5/50 |
| Tensile strain | |||
| Fracture, 3.20 mm, injection molded | 30 | % | ISO 527-2/5/50 |
| Bending modulus | |||
| injection molding | 2500 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method I (3 point load) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |