| About |
|---|
| SABIC® PPcompound G3135X is a 35% short glass fiber reinforced Polypropylene. This material has been designed for high stiffness, high impact, high heat resistance and chemical resistance. The glass fibres are chemically coupled to the PP matrix. Typical application of this material would include air inlet manifolds. The material is available in standard black. SABIC® PPcompound G3135X is a designated automotive grade.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,High Heat Resistance,Chemical coupling,Solvent resistance |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.17 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD：24 hrs | 0.40 | % | ISO 294-4 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 2.0 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23℃ | 107 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 4.0 | % | ISO 527-2 |
| Tensile modulus | |||
| 23℃ | 7725 | MPa | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 8070 | MPa | ISO 178 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 160 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, annealed | 152 | ℃ | ISO 75-2/Af |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 60.9 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| 23℃ | 14.9 | kJ/m² | ISO 179/1eA |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 3-point loading |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |