| SABIC® PPcompound G3230AE is a 30% short glass fiber reinforced Polypropylene for unter-the-hood and structural applications. The base material is a PP homopolymer, optimized for low emission values. The glass fibres are chemically coupled to the PP matrix. This material has been designed to combine a good performance profile with fast processing. SABIC® PPcompound G3230AE is a designated automotive grade.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Quick molding cycle,Low odor,Chemical coupling,Homopolymer |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 12 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| 24 hrs | 0.60 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23 ℃, 4 mm, injection molding | 6500 | MPa | ISO 527-2/1A/5 |
| tensile strength | |||
| Fracture, 4 mm, injection molded | 97.0 | MPa | ISO 527-2/1A/5 |
| Tensile strain | |||
| Fracture, 4 mm, injection molded | 3.7 | % | ISO 527-2/1A/5 |
| Bending modulus | |||
| injection molding | 6300 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23 ℃, injection molding | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23 ℃, injection molding | 53 | kJ/m² | ISO 179/1eU |
| Impact strength of cantilever beam notch | |||
| 23 ℃, injection molding | 12 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 150 | ℃ | ISO 75-2/A |
| Linear coefficient of thermal expansion | |||
| MD | ASTM D696 | ||
| -30 to 30 ℃ | 3.3E-5 | cm/cm/℃ | ASTM D696 |
| 23 to 80 ℃ | 3.1E-5 | cm/cm/℃ | ASTM D696 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 3-point loading |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |