| PS 330是高冲击聚苯乙烯的苯乙烯单体的质量连续聚合生产。在聚合过程中加入弹性体以达到抗冲击性能。它的颜色一般是不透明的。它是一种高抗冲击强度聚苯乙烯，具有较高的热变形温度和良好的物理性能。PS 330主要用于挤出和热成型应用。可用于食品包装和乳制品。 |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PS |
| Material Status | Commercial: Active |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 230℃，2.16kg | 4 | g/10min | ASTM D1238 |
| Polymer performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Load density | |||
| 23℃ | 1040 | kg/m³ | ASTM D792 |
| bulk density | |||
| Method B | 600 | kg/m³ | ASTM D 1895 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 29 | MPa | ASTM D638 |
| Tensile strain | 500 | % | ASTM D638 |
| Tensile modulus | 2353 | MPa | ASTM D638 |
| Bending strength | 44 | MPa | ASTM D790 |
| Bending modulus | 2647 | MPa | ASTM D790 |
| Rockwell hardness | 67 | ASTM D785 | |
| M-scale | 10 | – | ASTM D785 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level, UL 94 | |||
| @1.3 mm and 3 mm (natural color) | HB | Class | – |
| Vicat Softening Temp | 98 | ℃ | ASTM D1525 |
| Hot deformation temperature | |||
| 0.45 MPa, annealed | 97 | ℃ | ASTM D648 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 110 | J/m | ASTM D256 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |