| About |
|---|
| SABITAL™ 90GV10 is POM copolymer compounded with glass fibers for injection molding applications, it is reinforced with ca. 10% glass fibers for application requiring high stiffness, strength and thermal property. |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Copolymer Polyformaldehyde |
| Material Status | Commercial: Active |
| Features | Inoxidizability,Heat Resistance, Good |
| Availabilitys | Africa & Middle East ,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.48 | g/cm³ | ISO 1183 |
| Melt Volume Rate | 4.50 | cm³/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 4000 | MPa | ISO 527-2/1A/1 |
| Tensile stress (fracture) | 90.0 | MPa | ISO 527-2/1A/5 |
| Tensile strain | |||
| fracture | 3.5 | % | ISO 527-2/1A/5 |
| Bending modulus | |||
| 23℃ | 4000 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 35 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 154 | ℃ | ISO 75-2/A |
| Melting temperature | 166 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| MD | 6.0E-5 | 1/℃ | |
| TD | 1.2E-4 | 1/℃ |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |