| About |
|---|
| SABIC® SUPEER™ 8315 is an ethylene-octene copolymer produced via Nexlene™ Technology. It performs well in a wide range of general purpose and high performance LLDPE cast film applications and has good impact strength and transparency. Application Typical applications for SABIC® SUPEER™ 8315 are stretch wrap film and silage film. This product is not intended for and must not be used in any pharmaceutical/medical applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | mLLDPE |
| Material Status | Commercial: Active |
| Features | High impact resistance,Low density,Octene copolymer,Copolymer |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.915 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 3.0 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 40 | µm | |
| tensile strength | |||
| MD, yield, 40 µ m, blow molded film | 11.0 | MPa | |
| TD, yield, 40 µ m, blow molded film | 10.0 | MPa | |
| MD, fracture, 40 µ m, blow molded film | 48.0 | MPa | |
| TD, fracture, 40 µ m, blow molded film | 49.0 | MPa | |
| Tensile strain | |||
| MD, fracture, 40 µ m, extruded film | 600 | % | |
| TD, fracture, 40 µ m, extruded film | 700 | % | |
| Drop hammer impact | |||
| 40 µ m, cast thin film | 1000 | g | ASTM D1709 |
| Elmandorf tear strength | |||
| MD: 40 µ m, cast thin film | 11 | g | |
| TD: 40 µ m, cast thin film | 25 | g |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 113 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | |||
| 40 µ m, cast thin film | 1.5 | % | ASTM D1003 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| 250 to 300 | ℃ | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. F50 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |