SABIC® Vestolen A 5061R 10000

About
SABIC® Vestolen A 5061R 10000 (black) is a grade, which has a high density and a bimodal distribution of the molecular mass. An universal grade for pipe extrusion which, due to a keen combination of properties, is typically used for drinking water and waste water piping. This material meets (inter)national standards for use in drinking water and wastewater piping. MRS class ISO 12162 MPa = 8.0 (PE 80). This product is not intended for and must not be used in any pharmaceutical/medical applications.&&

About

SABIC® Vestolen A 5061R 10000 (black) is a grade, which has a high density and a bimodal distribution of the molecular mass. An universal grade for pipe extrusion which, due to a keen combination of properties, is typically used for drinking water and waste water piping. This material meets (inter)national standards for use in drinking water and wastewater piping. MRS class ISO 12162 MPa = 8.0 (PE 80). This product is not intended for and must not be used in any pharmaceutical/medical applications.&&

Product Description
Supplier	SABIC
Generic	HDPE
Material Status	Commercial: Active
Features	High density,Bimodal molecular weight distribution
Availabilitys	Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.958	g/cm³	ISO 1183
Melt Flow Rate			ISO 1133
190℃，2.16kg	0.10	g/10min
190℃，5.0kg	0.36	g/10min

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179/1eA
-30℃	8.6	kJ/m²
23℃	23	kJ/m²

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	70.0	℃	ISO 75-2/B
1.8 MPa, unannealed	42.0	℃	ISO 75-2/A
Vicat Softening Temp	70.0	℃	ISO 306/B
Melting temperature	123 to 127	℃	DIN 53765
Oxygen sensing time
210℃	> 20	min	ISO 11357-6

Supplementary information	Nominal value	Unit	Test method
Color Number（RAL）	9004
MRS Classification	8.00	MPa	ISO 12162

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D, molded	59		ISO 868
Tensile modulus
2 mm, molded into shape	1000	MPa	ISO 527-2/1BA/50
tensile strength
Yield, 2 mm, molded	23.0	MPa	ISO 527-2/1BA/50
Tensile strain
Yield, 2 mm, molded	9.0	%	ISO 527-2/1BA/50

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.