SABIC® Vestolen A 6060R 10000

About
SABIC® Vestolen A 6060R 10000 (black) is a grade which has a high density and a bimodal distribution of the molecular mass. Due to its profile of properties this material is typically used for gas and drinking water piping. This material meets (inter)national standards for use in gas, drinking water and waste water piping. MRS class ISO 12162 MPa = 10.0 (PE 100). This product is not intended for and must not be used in any pharmaceutical/medical applications.&&

About

SABIC® Vestolen A 6060R 10000 (black) is a grade which has a high density and a bimodal distribution of the molecular mass. Due to its profile of properties this material is typically used for gas and drinking water piping. This material meets (inter)national standards for use in gas, drinking water and waste water piping. MRS class ISO 12162 MPa = 10.0 (PE 100). This product is not intended for and must not be used in any pharmaceutical/medical applications.&&

Product Description
Supplier	SABIC
Generic	HDPE
Material Status	Commercial: Active
Features	High density,Bimodal molecular weight distribution
Availabilitys	Europe
Process Methods	Extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.959	g/cm³	ISO 1183
Melt Flow Rate			ISO 1133
190℃，2.16kg	0.10	g/10min	ISO 1133
190℃，5.0kg	0.30	g/10min	ISO 1133

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179/1eA
-30 ℃, molded	9.2	kJ/m²	ISO 179/1eA
23 ℃, molded	23	kJ/m²	ISO 179/1eA

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	72.0	℃	ISO 75-2/B
1.8 MPa, unannealed	43.0	℃	ISO 75-2/A
Vicat Softening Temp	71.0	℃	ISO 306/B
Melting temperature
DSC	124 to 128	℃	DIN 53765
Oxygen sensing time
Molded molding, 210 ℃	> 20	min	ISO 11357-6

Supplementary information	Nominal value	Unit	Test method
MRS Classification	10.0	MPa	ISO 12162
RAL Number	9004

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D, molded	59		ISO 868
Tensile modulus
2 mm, molded into shape	1050	MPa	ISO 527-2/1BA/50
tensile strength
Yield, 2 mm, molded	24.0	MPa	ISO 527-2/1BA/50
Tensile strain
Yield, 2 mm, molded	9.0	%	ISO 527-2/1BA/50

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.