SABIC® Vestolen A RELY 5922R 10000 Black

About
SABIC® Vestolen A RELY 5922R 10000 is a grade which has a high density and a bimodal distribution of the molecular mass. Due to its resistance against slow crack growth (SCG) the material SABIC® Vestolen A RELY 5922R 10000 is considered as PE100-RC and may be used for no dig applications. Moreover it may be used for the production of thick walled (large diameter and low SDR) pipes for infrastructure and industrial application due to its low sagging characteristics and it shows favorable processing behavior. This material meets (inter)national standards for use in gas, drinking water and waste water piping.MRS class ISO 12162 MPa = 10.0 (PE 100). This product is not intended for and must not be used in any pharmaceutical/medical applications.

About

SABIC® Vestolen A RELY 5922R 10000 is a grade which has a high density and a bimodal distribution of the molecular mass. Due to its resistance against slow crack growth (SCG) the material SABIC® Vestolen A RELY 5922R 10000 is considered as PE100-RC and may be used for no dig applications. Moreover it may be used for the production of thick walled (large diameter and low SDR) pipes for infrastructure and industrial application due to its low sagging characteristics and it shows favorable processing behavior. This material meets (inter)national standards for use in gas, drinking water and waste water piping.MRS class ISO 12162 MPa = 10.0 (PE 100). This product is not intended for and must not be used in any pharmaceutical/medical applications.

Product Description
Supplier	SABIC
Generic	HDPE
Material Status	Commercial: Active
Features	Good tear strength,High density,Bimodal molecular weight distribution
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.959	g/cm³	ASTM D1505
Melt Flow Rate
190℃，5.0kg	0.20	g/10min	ISO 1133
ESCR – Strain Hardening，Gp	> 50.0	MPa	Internal Method
Full incision creep test (80 ° C)	> 12.0	month	ISO 16770
Carbon black content	2.3	%	ISO 6964

IMPACT	Nominal value	Unit
Charpy Notched Impact Strength
-30℃	10	kJ/m²
23℃	26	kJ/m²

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	72.0	℃	ISO 75-2/B
1.8 MPa, unannealed	45.0	℃	ISO 75-2/A
Vicat Softening Temp	72.0	℃	ISO 306/B
Melting temperature	124 to 128	℃	DIN 53765
Oxygen induction time (210 ° C)	> 20	min	ISO 11357-6

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	62		ISO 868
Tensile modulus
2 mm	1100	MPa	ISO 527-2/1BA/50
Tensile stress (yield, 2.00 mm)	24.0	MPa	ISO 527-2/1BA/50
Tensile strain
Yield, 2 mm	9.0	%	ISO 527-2/1BA/50
Notch Pipe Test	> 12.0	month	EN ISO 13479

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.