| FORTIFY™ C5070是通过使用茂金属催化剂,采用溶液聚合法制备的乙烯辛烯共聚物。该产品可作为自由流动的球团。它作为一个低密度，高性能共聚物改性剂，具有优越的冲击特性和流动特性。 |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polyolefin Elastomer |
| Material Status | Commercial: Active |
| Features | High impact resistance,Good liquidity |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Shore hardness | |||
| Shore A, 1 second | 63 | ASTM D2240 | |
| Shore D, 1 second | 16 | ASTM D2240 | |
| tensile property | |||
| Breaking strength | 6 | MPa | ASTM D638 |
| Tensile strain | 1100 | % | ASTM D638 |
| Modulus 100% | 2.3 | MPa | ASTM D638 |
| Bending modulus | |||
| 1% tangent | 10.8 | MPa | ASTM D790-A |
| tear strength | |||
| C-type | 35.3 | kN/m | ASTM D624 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 0.868 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 5.0 | g/10min | ASTM D1238 |
| 230℃，2.16kg | 11.0 | g/10min | ASTM D1238 |
| Mooney viscosity | |||
| ML 1+4，121℃ | 8 | MU | ASTM D1646 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting peak temperature | 62 | ℃ | SABIC method |
| Glass transition temperature | -52 | ℃ | SABIC method |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |