| About |
|---|
| Safrene™ M 5010NAT100 High Density Polyethylene Resin is a high molecular mass grade developed for pressure pipe applications. It has good impact strength, abrasion and chemical resistance properties. Safrene™ M 5010NAT100 High Density Polyethylene Resin is a suitable for small and large diameter pressure pipe applications. It is also recommended for sheet extrusion.&& |
| Product Description | |
|---|---|
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | High impact resistance,Food contact compliance,High molecular weight,Good wear resistance,Solvent resistance |
| Availabilitys | Africa & Middle East |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.948 | g/cm³ | ISO 1183 |
| Melt Flow Rate | ISO 1133 | ||
| 190℃，21.6kg | 9.0 | g/10min | |
| 190℃，5.0kg | 0.25 | g/10min | |
| Viscosity value | |||
| Reduced viscosity | 340.0 | ml/g | ISO 1628 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30 ℃, molded | 4.0 | kJ/m² | |
| 23 ℃, molded | 12 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 67.0 | ℃ | ISO 306/B |
| Melting temperature | |||
| DSC | 130 to 133 | ℃ | ISO 3146 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, molded | 61 | ISO 868 | |
| tensile strength | ISO 527-2/50 | ||
| Yield, molding | 24.0 | MPa | |
| Fracture, molded | 35.0 | MPa | |
| Tensile strain | |||
| Fracture, molded | > 600 | % | ISO 527-2/50 |
| bending strength | |||
| 3.50% strain, molded | 19.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 180 to 200 | °C | |
| Barrel 2 zone temperature | 190 to 220 | °C | |
| Barrel 3 zone temperature | 190 to 210 | °C | |
| Melt temperature | 190 to 220 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |