Safron® C142-01N

About
Safron® C142-01N Polypropylene Resin is a nucleated high impact copolymer specially suited for the twin walled sheet market where its good compressive strength, combined with flexibility for easy stamping out of complex shapes, renders it useful for a wide application area. It is also suitable for profile extrusion. Safron® C142-01N Polypropylene Resin can also be used for the injection moulding of technical parts and thick wall applications requiring exceptional toughness especially at low temperatures. Typical Applications Twin walled sheet Technical injection moulded pans Solid sheet and profile extrusion&&

About

Safron® C142-01N Polypropylene Resin is a nucleated high impact copolymer specially suited for the twin walled sheet market where its good compressive strength, combined with flexibility for easy stamping out of complex shapes, renders it useful for a wide application area. It is also suitable for profile extrusion. Safron® C142-01N Polypropylene Resin can also be used for the injection moulding of technical parts and thick wall applications requiring exceptional toughness especially at low temperatures. Typical Applications Twin walled sheet Technical injection moulded pans Solid sheet and profile extrusion&&

Product Description
Generic	PP homopolymerization
Material Status	Commercial: Active
Features	Good flexibility,High impact resistance,Nucleation,Food contact compliance,Good compressive strength,Low temperature toughness,Impact copolymer
Availabilitys	Africa & Middle East
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.910	g/cm³	ISO 1183
Melt Flow Rate
230℃，2.16kg	1.4	g/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
tensile strength
Yield, injection molding	26.0	MPa	ISO 527-2
Tensile strain
Yield, injection molding	7.0	%	ISO 527-2
Bending modulus
injection molding	1200	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength			ISO 179
-20 ℃, injection molding	5.0	kJ/m²
0 ℃, injection molding	7.0	kJ/m²

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	74.0	℃	ISO 75-2/B
1.8 MPa, unannealed	52.0	℃	ISO 75-2/A
Vicat Softening Temp	71.0	℃	ISO 306/B

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.