Safron® H504-12M

About
Safron® H504-12M Polypropylene Resin is recommended for the spinning of staple fibre in the range 2 — 25 denier. It is also used for the manufacture of BCF yarns. Safron® H504-12M Polypropylene Resin is a medium to high flow injection moulding grade for applications where rigidity and fast cycle times are essential. Typical Process Applications High tenacity yarns Staple fibres End Use Applications Needle punched floor coverings Tufted carpets&&

About

Safron® H504-12M Polypropylene Resin is recommended for the spinning of staple fibre in the range 2 — 25 denier. It is also used for the manufacture of BCF yarns. Safron® H504-12M Polypropylene Resin is a medium to high flow injection moulding grade for applications where rigidity and fast cycle times are essential. Typical Process Applications High tenacity yarns Staple fibres End Use Applications Needle punched floor coverings Tufted carpets&&

Product Description
Generic	PP homopolymerization
Material Status	Commercial: Active
Features	Good liquidity,Quick molding cycle,Food contact compliance,Homopolymer
Availabilitys	Africa & Middle East
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.900	g/cm³	ISO 1183
Melt Flow Rate
230℃，2.16kg	12	g/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
tensile strength
Yield, injection molding	30.0	MPa	ISO 527-2
Tensile strain
Yield, injection molding	7.5	%	ISO 527-2
Bending modulus
injection molding	1360	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
23 ℃, injection molding	2.3	kJ/m²	ISO 179

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	83.0	℃	ISO 75-2/B
1.8 MPa, unannealed	55.0	℃	ISO 75-2/A
Vicat Softening Temp	85.0	℃	ISO 306/B

Process Conditions
injection	Nominal value	Unit	Test method
Extrusion	Nominal value	Unit	Test method
Barrel rear temperature	180 to 200	°C
Barrel middle temperature	220 to 260	°C
Barrel front temperature	250	°C
Nozzle temperature	240	°C
Barrel 1 zone temperature	180 to 240	°C
Barrel 2 zone temperature	230 to 250	°C
Barrel 3 zone temperature	240 to 270	°C
Barrel 4 zone temperature	270	°C
Nozzle temperature	240 to 260	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.