| About |
|---|
| 5000(+) is halogen-free flame retardant polypropylene with phosphorus and nitrogen as the flame retardant elements. Carbonize and expansion mechanism play the flame retardant performance. The flammability can reach UL94-V0 (0.75mm, 1.5mm and 3.0mm), and passed 70°Cx168 hours water immersion test (UL746C), glow-wire test meets GWIT750°C and GWFI960°C. 5000(+) has the characteristics of low density of finished products, low smoke, less corrosion to the mould etc. 5000(+) halogen free flame retardant PP have UL certification, and meet the requirements of RoHS, SVHC, PFOS & PFOA, 16P, Halogen-free, PAHs…etc.&& |
| Product Description | |
|---|---|
| Supplier | POLYROCKS |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Low smoke,Halogen free,Corrosion Resistant,Flame Characteristics,Low density,V-0 |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.06 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 10 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 16.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 300 | % | ASTM D638 |
| Bending modulus | 1560 | MPa | ASTM D790 |
| bending strength | 25.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 85 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 115 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 , UL 746C | ||
| 0.75 mm | V-0 | UL 94 , UL 746C | |
| 1.50 mm | V-0 | UL 94 , UL 746C | |
| 3.00 mm | V-0 | UL 94 , UL 746C |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90 | °C | |
| Drying time | 2.0 | hr | |
| Processing (melt) temperature | 180 to 200 | °C | |
| Mold temperature | 40 to 70 | °C | |
| Notes |
|---|
| 1. Phosphorus and Nitrogen |
| 2. Typical properties: these are not to be construed as specifications. |
| 3. After 70°Cx168h water immersion test |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |