SAMAT 5003N5 - SOLIAO

About
SAMAT™ 5003N (+) are halogen-free environmental polypropylene (PP) with phosphorus and nitrogen as the flame retardant elements. The synergistic effect of coagulation phase and gas phase on flame retardation enhances the flame retardant efficiency, and the catalytic mechanism accelerates the melting and dropping of the system. The flammability can reach UL94-V2 (0.75mm,1.5mm and 3.0mm) and pass the water immersion test at 70°C for 168hrs (UL746C) and GWIT 750°C and GWFI 960°. They have the characteristics of low density of finished products, low smoke and little corrosion to molds. 5003N (+) pass UL tests and meet the requirements of RoHS, SVHC, PFOS&PFOA, 16P, Halogen-free and PAHs.&&

About

SAMAT™ 5003N (+) are halogen-free environmental polypropylene (PP) with phosphorus and nitrogen as the flame retardant elements. The synergistic effect of coagulation phase and gas phase on flame retardation enhances the flame retardant efficiency, and the catalytic mechanism accelerates the melting and dropping of the system. The flammability can reach UL94-V2 (0.75mm,1.5mm and 3.0mm) and pass the water immersion test at 70°C for 168hrs (UL746C) and GWIT 750°C and GWFI 960°. They have the characteristics of low density of finished products, low smoke and little corrosion to molds. 5003N (+) pass UL tests and meet the requirements of RoHS, SVHC, PFOS&PFOA, 16P, Halogen-free and PAHs.&&

Product Description
Supplier	POLYROCKS
Generic	PP not specified
Material Status	Commercial: Active
Features	Low smoke,Halogen free,Corrosion Resistant,Flame Characteristics,Low density,V-2
Availabilitys	Asia Pacific

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.10	g/cm³	ASTM D792
Melt Flow Rate
230℃，2.16kg	10	g/10min	ASTM D1238

MECHANICAL	Nominal value	Unit	Test method
tensile strength
yield	30.0	MPa	ASTM D638
Tensile strain
fracture	70	%	ASTM D638
Bending modulus	1700	MPa	ASTM D790
bending strength	38.0	MPa	ASTM D790

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	70	J/m	ASTM D256

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level			UL 746C, UL 94
0.75 mm	V-2
1.50 mm	V-2
3.00 mm	V-2
Glowing wire flammability index	960	℃	IEC 60695-2-12
Igniting temperature of the hot wire	750	℃	IEC 60695-2-13

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	90.0	°C
Drying time	2.0	hr
Processing (melt) temperature	180 to 200	°C
Mold temperature	40.0 to 70.0	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.