| 5003S(+) is low halogen flame retardant PP with phosphorus, nitrogen and bromine as main flame retardant elements. It improves flame retardant efficiency by synergistic effect of solidifying phase and gas-phase mechanism,and accelerating melting and dripping by catalytic mechanism to play flame retardant perforamnce. 5003S(+) flammability can reach UL94-V2(1.5mm and 3.0mm), glow-wire test meets GWIT 750°C and GWFI 850°C. 5003S(+) have UL certification, and meet the requirements of RoHS, SVHC, PFOS & PFOA, 16P, Halogen-free, PAHs…etc. 5003S(+) has the characteristics of low smoke, low density of finished products, less corrosion to the mould etc.&& |
| Product Description | |
|---|---|
| Supplier | POLYROCKS |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Low Halogen Content,Low smoke,Corrosion Resistant,Flame Characteristics,Low density,V-2 |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.910 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 12 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 28.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 200 | % | ASTM D638 |
| Bending modulus | 1100 | MPa | ASTM D790 |
| bending strength | 30.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 70 | J/m | ASTM D256 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | V-2 | UL 94 | |
| 3.00 mm | V-2 | UL 94 | |
| Glowing wire flammability index | 850 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | 750 | ℃ | IEC 60695-2-13 |
| Notes |
|---|
| 1. Phosphorus, Nitrogen and Bromine |
| 2. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |