| About |
|---|
| A soft, black, versatile thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material combines good physical properties and chemical resistance for use in a wide range of applications. This grade of Santoprene TPV is shear-dependent and can be processed on conventional thermoplastics equipment for injection molding or extrusion. It is polyolefin based and recyclable within the manufacturing stream.&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Material Status | Commercial: Active |
| Features | Solvent resistance,Good heat aging resistance,Ozone resistance,Good flexibility,Renewable resources,Insulation,Good Electrical Properties,HB,Fatigue resistance,Good Dimensional Stability |
| Availabilitys | Africa & Middle East ,North America,Europe,Asia Pacific,Latin America |
| Process Methods | Profile extrusion,Multiple injection molding,Injection Molding,Extrusion |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile Strength | |||
| 100% stretch elongation, vertical perpendicular | 1.88 | MPa | ISO 527-2 |
| Broken BRK, vertical perpendicular | 5.01 | MPa | ISO 527-2 |
| Elongation at Break | |||
| Vertical vertical | 420 | % | ISO 527-1,2 |
| Shore hardness | |||
| 15 s | 60 | Shore A | ISO 868 |
| Changes after aging | -1 | Shore A | ISO 868 |
| 70℃，24 h | 23 | % | ISO 815 |
| 125℃，70h | 35 | % | ISO 815 |
| Tear strength | |||
| Vertical normal | 17.9 | kN/m | ISO 34-1 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Brittle Temperature | |||
| -60 | ℃ | ISO 974 | |
| -60 | ℃ | ASTM D746 | |
| Relative Temperature Index (RTI) | |||
| electrical | |||
| 1.5 mm | 90 | ℃ | UL-746B |
| 3.0 mm | 90 | ℃ | UL-746B |
| Strength | |||
| 1.5 mm | 90 | ℃ | UL-746B |
| 3.0 mm | 95 | ℃ | UL-746B |
| Supplementary Information | Nominal value | Unit | Test method |
|---|---|---|---|
| Continuous Upper Temperature Resistance | |||
| 1000h | 135 | ℃ | SAE J2236 |
| Detergent resistance | |||
| f3 | UL 749 | ||
| f4 | UL 2157 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| 1.5 mm | HB | calss | UL 94 |
| 1.0 mm | HB | calss | UL 94 |
| Hot wire ignition | |||
| 1 mm | PLC4 | s | UL 746A |
| 1.5 mm | PLC3 | s | UL 746A |
| 3 mm | PLC3 | s | UL 746A |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Relative permittivity | 2.4 | IEC 62631-2-1 | |
| Compared Tracking Index | PLC 0 | PLC Code | UL 746 |
| Arc Resistance | PLC 6 | class | UL 746 |
| Electric strength | 27 | kV/mm | ASTM D 149 |
| High Amperage Arc Ignition Resistance | |||
| 1.5 mm | PLC 0 | arcs | UL 746A |
| High Amperage Arc Ignition Category | |||
| 1.5 mm | PLC 0 | class | UL 746A |
| High Voltage Arc Track Rate | PLC 1 | mm/min | UL 746A |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 960 | kg/m³ | ISO 1183 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion Molded | Nominal value | Unit | Test method |
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 82 | ℃ | |
| Drying Time | 3 | hr | |
| Melt Temperature | 196 | ℃ | |
| Drying Temperature | 82 | ℃ | |
| Drying Time | 3 | hr | |
| Maximum Moisture Content | 0.08 | % | |
| Maximum regrind level | 20 | % | |
| Melt Temperature | 215 | ℃ | |
| Mold Temperature | 10-52 | ℃ | |
| Vent Depth | 25 | μm | |
| Back Pressure | 0.345-0.689 | MPa | |
| Injection speed | 快速 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die C |
| 3. Method Bb, Angle (Nicked) |
| 4. Type 1 |
| 5. Type A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |