| About |
|---|
| A hard, black, versatile thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material combines good physical properties and chemical resistance for use in a wide range of applications. This grade of Santoprene TPV is shear-dependent and can be processed on conventional thermoplastics equipment for injection molding, extrusion, blow molding, thermoforming or vacuum forming. It is polyolefin based and recyclable within the manufacturing stream.&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Material Status | Commercial: Active |
| Features | Renewable resources,Fatigue resistance,Ozone resistance,Good Electrical Properties,Solvent resistance,Good Dimensional Stability,Good tear strength,Insulation |
| Availabilitys | Asia Pacific,Africa & Middle East ,Latin America,North America,Europe |
| Process Methods | Injection Molding,Thermo forming,Profile extrusion,Extrusion,Multiple injection molding |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile Strength | |||
| 100% elongation, vertical perpendicular | 9 | MPa | ISO 527-2 |
| Broken BRK, vertical perpendicular | 20.7 | MPa | ISO 527-2 |
| Elongation at Break | 610 | % | ISO 527-1,2 |
| Shore hardness | 41 | Shore A | ISO 868 |
| 70℃，24h | 54 | % | ISO 815 |
| 125℃，70h | 61 | % | ISO 815 |
| Tear strength | 64 | kN/m | ISO 34-1 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Brittle Temperature | -52 | ℃ | ASTM D746 |
| Low temperature brittleness | -52 | ℃ | ISO 812 |
| Relative Temperature Index (RTI) | |||
| Electrical Elec | |||
| 1.5 mm | 85 | ℃ | UL-746B |
| 3.0 mm | 85 | ℃ | UL-746B |
| Strengthen str | |||
| 1.5 mm | 85 | ℃ | UL-746B |
| 3.0 mm | 85 | ℃ | UL-746B |
| Aging property | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness change after aging | 4 | ISO 868 |
| Supplementary Information | Nominal value | Unit | Test method |
|---|---|---|---|
| Detergent resistance | f3 | UL 749 | |
| Detergent resistance | f4 | UL 2157 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| 1.5 mm | HB | calss | UL 94 |
| 1.0 mm | HB | calss | UL 94 |
| Hot wire ignition | |||
| 1 mm | PLC 4 | s | UL 746A |
| 1.5 mm | PLC 3 | s | UL 746A |
| 3 mm | PLC 2 | s | UL 746A |
| ELECTRICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Relative permittivity | 2.6 | IEC 62631-2-1 | |
| Compared Tracking Index | 0 | PLC Code | UL 746A |
| Arc Resistance | 5 | PLC Code | UL 746B |
| Electric strength | 32 | kV/mm | ASTM D149 |
| High Arc Burning Index (HAI) | 0 | PLC Code | UL 746A |
| High Voltage Arc Track Rate | 1 | mm/min | UL 746A |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 950 | kg/m³ | ISO 1183 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion Molded | Nominal value | Unit | Test method |
| Injection Molding | Nominal value | Unit | Test method |
| Drying Temperature | 82 | ℃ | |
| Drying Time | 3 | hr | |
| Melt Temperature | 210 | ℃ | |
| Drying Temperature | 82 | ℃ | |
| Drying Time | 3 | hr | |
| Maximum Moisture Content | 0.08 | % | |
| Maximum regrind level | 20 | % | |
| Melt Temperature | 215 | ℃ | |
| Mold Temperature | 10-52 | ℃ | |
| Vent Depth | 25 | μm | |
| Back Pressure | 0.345-0.689 | MPa | |
| Injection speed | 快速 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die C |
| 3. Method Bb, Angle (Nicked) |
| 4. Type 1 |
| 5. Type A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |