| About |
|---|
| A soft, black, UV resistant thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material is designed for automotive interior applications requiring low fogging and good appearance. This grade of Santoprene TPV is shear-dependent and can be processed on conventional thermoplastics equipment for injection molding. It is polyolefin based and recyclable within the manufacturing stream.&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Material Status | Commercial: Active |
| Features | Ozone resistance,Weather resistance is good,Renewable resources,Good surface appearance,Good Dimensional Stability,Solvent resistance,High liquidity |
| Availabilitys | Europe,Latin America,North America,Asia Pacific,Africa & Middle East |
| Process Methods | Injection Molding,Multiple injection molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.918 | g/cm³ | ASTM D792 |
| Density | 0.920 | g/cm³ | ISO 1183 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| TD, fracture, 23 ℃ | 6.60 | MPa | ISO 37 |
| TD, fracture, 23 ℃ | 6.60 | MPa | ASTM D412 |
| TD, 100% strain, 23 ℃ | 2.30 | MPa | ISO 37 |
| TD, 100% strain, 23 ℃ | 2.30 | MPa | ASTM D412 |
| Tensile strain | |||
| TD, fracture, 23 ℃ | 490 | % | ISO 37 |
| TD, fracture, 23 ℃ | 490 | % | ASTM D412 |
| Compression deformation | ASTM D395B | ||
| 70℃，22 hr | 41 | % | ASTM D395B |
| 100℃，70 hr | 53 | % | ASTM D395B |
| Compression deformation | ISO 815 | ||
| 70℃，22 hr | 41 | % | ISO 815 |
| 100℃，70 hr | 53 | % | ISO 815 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 15 seconds, 23 ℃ | 65 | ISO 868 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -52.0 | ℃ | ASTM D746 |
| Embrittlement temperature | -52.0 | ℃ | ISO 812 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| The rate of change in tensile strength in air (100 ℃, 1008 hr) | -3.0 | % | ASTM D573 |
| The rate of change in tensile strength in air (100 ℃, 1008 hr) | -3.0 | % | ISO 188 |
| The rate of change in ultimate elongation in air | |||
| 100℃，1008 hr | -10 | % | ASTM D573 |
| Change in Tensile Strain at Break in Air（100℃，1008 hr） | -10 | % | ISO 188 |
| Change in Durometer Hardness in Air (100 ℃, 1008 hr) | 2.0 | ASTM D573 | |
| The rate of change of Shore hardness in air | |||
| Shore A, 100 ℃, 1008 hr | 2.0 | ISO 188 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type 1 |
| 3. Type A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |