| About |
|---|
| A soft, black, UV resistant thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material combines good physical properties and chemical resistance, and is designed for thin wall or complex profile extrusion applications. This grade of Santoprene TPV is shear-dependent and can be processed on conventional thermoplastics equipment for extrusion, thermoforming or vacuum forming. It is polyolefin based and recyclable within the manufacturing stream.&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Material Status | Commercial: Active |
| Features | HB,Renewable resources,Good melt strength,Ozone resistance,Solvent resistance,Weather resistance is good,Good Dimensional Stability |
| Availabilitys | Europe,Asia Pacific,North America,Africa & Middle East ,Latin America |
| Process Methods | Thermo forming,Profile extrusion,Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.968 | g/cm³ | ASTM D792 |
| Density | 0.970 | g/cm³ | ISO 1183 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| TD, fracture, 23 ℃ | 8.80 | MPa | ASTM D412 |
| TD, fracture, 23 ℃ | 8.80 | MPa | ISO 37 |
| TD, 100% strain, 23 ℃ | 3.50 | MPa | ISO 37 |
| TD, 100% strain, 23 ℃ | 3.50 | MPa | ASTM D412 |
| Tensile strain | |||
| TD, fracture, 23 ℃ | 460 | % | ASTM D412 |
| TD, fracture, 23 ℃ | 460 | % | ISO 37 |
| tear strength | |||
| TD，23℃ | 24.0 | kN/m | ASTM D624 |
| TD，23℃ | 24 | kN/m | ISO 34-1 |
| Compression deformation | ASTM D395B | ||
| 70℃，22 hr | 33 | % | ASTM D395B |
| 125℃，70 hr | 42 | % | ASTM D395B |
| Compression deformation | ISO 815 | ||
| 70℃，22 hr | 33 | % | ISO 815 |
| 125℃，70 hr | 42 | % | ISO 815 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 15 seconds, 23 ℃ | 78 | ISO 868 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -60.0 | ℃ | ASTM D746 |
| Embrittlement temperature | -60.0 | ℃ | ISO 812 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| The rate of change in tensile strength in air | |||
| 150℃，168 hr | -9.0 | % | ASTM D573 |
| 150℃，168 hr | -9.0 | % | ISO 188 |
| The rate of change in ultimate elongation in air | |||
| 150℃，168 hr | -2.0 | % | ASTM D573 |
| Change in Tensile Strain at Break in Air（150℃，168 hr） | -2.0 | % | ISO 188 |
| Change in Durometer Hardness in Air (150 ℃, 168 hr) | 5.0 | ASTM D573 | |
| The rate of change of Shore hardness in air | |||
| Shaw A, 150 ℃, 168 hr | 5.0 | ISO 188 | |
| The rate of change in tensile strength | |||
| 125℃，70 hr，in IRM 903 Oil | -39 | % | ASTM D471 |
| Change in Tensile Stress（125℃，70 hr，in IRM 903 Oil） | -39 | % | ISO 1817 |
| Change in Ultimate Elongation（125℃，70 hr，in IRM 903 Oil） | -54 | % | ASTM D471 |
| Change in Tensile Strain at Break（125℃，70 hr，in IRM 903 Oil） | -54 | % | ISO 1817 |
| Volume change | |||
| 125 ℃, 70 hr, in IRM 903 oil | 79 | % | ASTM D471 |
| 125 ℃, 70 hr, in IRM 903 oil | 79 | % | ISO 1817 |
| Durable to continuous maximum temperature | |||
| 1008 hr | 135 | ℃ | SAE J2236 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | |||
| 23 ℃，2 mm | 27 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 23 ℃，1.98 mm | 2.70 | ASTM D150 | |
| 23 ℃，1.98 mm | 2.70 | IEC 60250 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.00 mm | HB | UL 94 | |
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 82 | °C | |
| Drying time | 3.0 | hr | |
| Melt temperature | 177 to 204 | °C | |
| Nozzle temperature | 204 | °C | |
| Back pressure | 5.00 to 20.0 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die C |
| 3. Method Bb, Angle (Nicked) |
| 4. Type 1 |
| 5. Type A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |