| About |
|---|
| A soft, black, UV resistant thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material combines good physical properties and chemical resistance for use in difficult injection molding applications. This grade of Santoprene TPV is shear-dependent and can be processed on conventional thermoplastics equipment for injection molding. It is polyolefin based and recyclable within the manufacturing stream.&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Material Status | Commercial: Active |
| Features | Good Dimensional Stability,Ozone resistance,Renewable resources,HB,Good surface appearance,Solvent resistance,Weather resistance is good,Fatigue resistance,High liquidity,Excellent Processability |
| Availabilitys | North America,Asia Pacific,Latin America,Africa & Middle East ,Europe |
| Process Methods | Multiple injection molding,Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.918 | g/cm³ | ASTM D792 |
| Density | 0.920 | g/cm³ | ISO 1183 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| TD, fracture, 23 ℃ | 7.00 | MPa | ISO 37 |
| TD, fracture, 23 ℃ | 7.00 | MPa | ASTM D412 |
| TD, 100% strain, 23 ℃ | 3.50 | MPa | ASTM D412 |
| TD, 100% strain, 23 ℃ | 3.50 | MPa | ISO 37 |
| Tensile strain | |||
| TD, fracture, 23 ℃ | 480 | % | ISO 37 |
| TD, fracture, 23 ℃ | 480 | % | ASTM D412 |
| tear strength | |||
| TD，23℃ | 26.0 | kN/m | ASTM D624 |
| TD，23℃ | 26 | kN/m | ISO 34-1 |
| Compression deformation | ASTM D395B | ||
| 70℃，22 hr | 40 | % | ASTM D395B |
| 125℃，70 hr | 53 | % | ASTM D395B |
| Compression deformation | ISO 815 | ||
| 70℃，22 hr | 40 | % | ISO 815 |
| 125℃，70 hr | 53 | % | ISO 815 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 15 seconds, 23 ℃ | 80 | ISO 868 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -60.0 | ℃ | ASTM D746 |
| Embrittlement temperature | -60.0 | ℃ | ISO 812 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| The rate of change in tensile strength in air | |||
| 150℃，168 hr | -11 | % | ISO 188 |
| 150℃，168 hr | -11 | % | ASTM D573 |
| The rate of change in ultimate elongation in air | |||
| 150℃，168 hr | -14 | % | ASTM D573 |
| Change in Tensile Strain at Break in Air（150℃，168 hr） | -14 | % | ISO 188 |
| Change in Durometer Hardness in Air (150 ℃, 168 hr) | 2.0 | ASTM D573 | |
| The rate of change of Shore hardness in air | |||
| Shaw A, 150 ℃, 168 hr | 2.0 | ISO 188 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.10 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 | °C | |
| Drying time | 3.0 | hr | |
| Recommended maximum moisture content | 0.080 | % | |
| Proposed maximum recycled material ratio | 20 | % | |
| Barrel rear temperature | 182 | °C | |
| Barrel middle temperature | 188 | °C | |
| Barrel front temperature | 193 | °C | |
| Nozzle temperature | 199 | °C | |
| Processing (melt) temperature | 204 to 232 | °C | |
| Mold temperature | 10 to 52 | °C | |
| Injection speed | Fast | ||
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 100 to 200 | rpm | |
| Clamping force | 4.1 to 6.9 | kN/cm² | |
| Cushion | 3.18 to 6.35 | mm | |
| Screw length to diameter ratio | 16.0:1.0 to 20.0:1.0 | ||
| Screw compression ratio | 2.0:1.0 to 2.5:1.0 | ||
| Vent depth | 0.025 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die C |
| 3. Method Bb, Angle (Nicked) |
| 4. Type 1 |
| 5. Type A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |