| 它是热塑性弹性体（TPE）系列中的一种软质、黑色、抗紫外辐射的热塑性硫化弹 性体（TPV）。这种材料适用于要求低雾化和良好外观的汽车内饰应用。这一牌号 的山都平 TPV 是剪切速率依赖型产品，可在常规热塑性注塑成型设备上加工。这 是一种聚烯烃基材料，可在生产过程中进行回收利用。&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Material Status | Commercial: Active |
| Features | Solvent resistance,Good Dimensional Stability,Renewable resources,Weather resistance is good,High liquidity,Good surface appearance,Ozone resistance |
| Availabilitys | Europe,Latin America,Asia Pacific,Africa & Middle East ,North America |
| Process Methods | Multiple injection molding,Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.918 | g/cm³ | ASTM D792 |
| Density | 0.920 | g/cm³ | ISO 1183 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| TD, fracture, 23 ℃ | 11.0 | MPa | ASTM D412 |
| TD, fracture, 23 ℃ | 11.0 | MPa | ISO 37 |
| TD, 100% strain, 23 ℃ | 3.80 | MPa | ISO 37 |
| TD, 100% strain, 23 ℃ | 3.80 | MPa | ASTM D412 |
| Tensile strain | |||
| TD, fracture, 23 ℃ | 560 | % | ASTM D412 |
| TD, fracture, 23 ℃ | 560 | % | ISO 37 |
| Compression deformation | ASTM D395B | ||
| 70℃，22 hr | 53 | % | ASTM D395B |
| 100℃，70 hr | 56 | % | ASTM D395B |
| Compression deformation | ISO 815 | ||
| 70℃，22 hr | 53 | % | ISO 815 |
| 100℃，70 hr | 56 | % | ISO 815 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 15 seconds, 23 ℃ | 82 | ISO 868 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -58.0 | ℃ | ASTM D746 |
| Embrittlement temperature | -58.0 | ℃ | ISO 812 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| The rate of change in tensile strength in air (100 ℃, 1008 hr) | -7.0 | % | ASTM D573 |
| The rate of change in tensile strength in air (100 ℃, 1008 hr) | -7.0 | % | ISO 188 |
| The rate of change in ultimate elongation in air | |||
| 100℃，1008 hr | -8.0 | % | ASTM D573 |
| Change in Tensile Strain at Break in Air（100℃，1008 hr） | -8.0 | % | ISO 188 |
| Change in Durometer Hardness in Air (100 ℃, 1008 hr) | 2.0 | ASTM D573 | |
| The rate of change of Shore hardness in air | |||
| Shore A, 100 ℃, 1008 hr | 2.0 | ISO 188 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |