| A soft, colorable, specialty thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. It is designed for use in plumbing applications requiring potable water contact and also for food processing equipment. This grade of Santoprene TPV is shear-dependent and can be processed on conventional thermoplastics equipment for injection molding, extrusion or blow molding. It is polyolefin based and recyclable within the manufacturing stream.&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Material Status | Commercial: Active |
| Features | HB,Solvent resistance,Good coloring,Good heat aging resistance,Low temperature toughness,Good Dimensional Stability,Renewable resources,Ozone resistance,Fatigue resistance |
| Availabilitys | Latin America,Asia Pacific,North America,Europe,Africa & Middle East |
| Process Methods | Multiple injection molding,Extrusion,Profile extrusion,Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.968 | g/cm³ | ASTM D792 |
| Density | 0.970 | g/cm³ | ISO 1183 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| TD, fracture, 23 ℃ | 7.00 | MPa | ASTM D412 |
| TD, fracture, 23 ℃ | 7.00 | MPa | ISO 37 |
| TD, 100% strain, 23 ℃ | 2.60 | MPa | ISO 37 |
| TD, 100% strain, 23 ℃ | 2.60 | MPa | ASTM D412 |
| Tensile strain | |||
| TD, fracture, 23 ℃ | 450 | % | ISO 37 |
| TD, fracture, 23 ℃ | 450 | % | ASTM D412 |
| Compression deformation | ASTM D395B | ||
| 23℃，168 hr | 18 | % | ASTM D395B |
| 100℃，168 hr | 48 | % | ASTM D395B |
| Compression deformation | ISO 815 | ||
| 23℃，168 hr | 18 | % | ISO 815 |
| 100℃，168 hr | 48 | % | ISO 815 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 15 seconds, 23 ℃ | 69 | ISO 868 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Relative temperature index | |||
| Electrical performance | 100 | ℃ | UL 746 |
| Strength mechanical performance | 90.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | PLC 0 | UL 746 | |
| High Arc Burning Index (HAI) | PLC 0 | UL 746 | |
| High voltage arc ignition resistance index (HVAR) (PLC) | PLC 6 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 3 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 2 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.00 mm | HB | UL 94 | |
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 82 | °C | |
| Drying time | 3.0 | hr | |
| Recommended maximum moisture content | 0.080 | % | |
| Proposed maximum recycled material ratio | 20 | % | |
| Barrel rear temperature | 177 | °C | |
| Barrel middle temperature | 182 | °C | |
| Barrel front temperature | 182 | °C | |
| Nozzle temperature | 188 to 221 | °C | |
| Processing (melt) temperature | 193 to 232 | °C | |
| Mold temperature | 10 to 52 | °C | |
| Injection speed | Fast | ||
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 100 to 200 | rpm | |
| Clamping force | 4.1 to 6.9 | kN/cm² | |
| Cushion | 3.18 to 6.35 | mm | |
| Screw length to diameter ratio | 16.0:1.0 to 20.0:1.0 | ||
| Screw compression ratio | 2.0:1.0 to 2.5:1.0 | ||
| Vent depth | 0.025 | mm | |
| Drying temperature | 82 | °C | |
| Drying time | 3.0 | hr | |
| Melt temperature | 196 | °C | |
| Nozzle temperature | 199 | °C | |
| Back pressure | 5.00 to 20.0 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type 1 |
| 3. Type A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |