| A soft, colorable, specialty thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. It is designed for use in plumbing applications in contact with potable water. This grade of Santoprene TPV is shear-dependent and can be processed on conventional thermoplastics equipment for injection molding, extrusion, blow molding, thermoforming or vacuum forming. It is polyolefin based and recyclable within the manufacturing stream.&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Material Status | Commercial: Active |
| Features | Solvent resistance,Copper contact stability,Good heat aging resistance,Good coloring,Fatigue resistance,Renewable resources,Ozone resistance,Good Dimensional Stability,Low temperature toughness |
| Availabilitys | Europe,Latin America,North America,Asia Pacific,Africa & Middle East |
| Process Methods | Injection Molding,Extrusion,Profile extrusion,Multiple injection molding,Thermo forming |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.968 | g/cm³ | ASTM D792 |
| Density | 0.970 | g/cm³ | ISO 1183 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| TD, fracture, 23 ℃ | 8.80 | MPa | ASTM D412 |
| TD, fracture, 23 ℃ | 8.80 | MPa | ISO 37 |
| TD, 100% strain, 23 ℃ | 3.60 | MPa | ISO 37 |
| TD, 100% strain, 23 ℃ | 3.60 | MPa | ASTM D412 |
| Tensile strain | |||
| TD, fracture, 23 ℃ | 490 | % | ASTM D412 |
| TD, fracture, 23 ℃ | 490 | % | ISO 37 |
| Compression deformation | ASTM D395B | ||
| 23℃，168 hr | 25 | % | ASTM D395B |
| 100℃，168 hr | 57 | % | ASTM D395B |
| Compression deformation | ISO 815 | ||
| 23℃，168 hr | 25 | % | ISO 815 |
| 100℃，168 hr | 57 | % | ISO 815 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 15 seconds, 23 ℃ | 79 | ISO 868 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 82 | °C | |
| Drying time | 3.0 | hr | |
| Recommended maximum moisture content | 0.080 | % | |
| Proposed maximum recycled material ratio | 20 | % | |
| Barrel rear temperature | 177 | °C | |
| Barrel middle temperature | 182 | °C | |
| Barrel front temperature | 188 | °C | |
| Nozzle temperature | 193 to 227 | °C | |
| Processing (melt) temperature | 199 to 232 | °C | |
| Mold temperature | 10 to 52 | °C | |
| Injection speed | Fast | ||
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 100 to 200 | rpm | |
| Clamping force | 4.1 to 6.9 | kN/cm² | |
| Cushion | 3.18 to 6.35 | mm | |
| Screw length to diameter ratio | 16.0:1.0 to 20.0:1.0 | ||
| Screw compression ratio | 2.0:1.0 to 2.5:1.0 | ||
| Vent depth | 0.025 | mm | |
| Drying temperature | 82 | °C | |
| Drying time | 3.0 | hr | |
| Melt temperature | 202 | °C | |
| Nozzle temperature | 204 | °C | |
| Back pressure | 5.00 to 20.0 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type 1 |
| 3. Type A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |