| About |
|---|
| A soft, colorable, flame retardant thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material has good fluid resistance and contains non-ether brominated flame retardants. It does not contain metal deactivators. This grade of Santoprene TPV is shear-dependent and can be processed on conventional thermoplastics equipment for injection molding, extrusion, blow molding, thermoforming or vacuum forming. It is polyolefin based and recyclable within the manufacturing stream.&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Material Status | Commercial: Active |
| Features | Low temperature toughness,Good Electrical Properties,Solvent resistance,Good Dimensional Stability,Flame Characteristics,V-0,Fatigue resistance,Good heat aging resistance,Ozone resistance,Good coloring,Renewable resources |
| Availabilitys | Asia Pacific,Africa & Middle East ,North America,Latin America,Europe |
| Process Methods | Multiple injection molding,Injection Molding,Thermo forming,Profile extrusion,Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.24 | g/cm³ | ASTM D792 |
| Density | 1.24 | g/cm³ | ISO 1183 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| TD, fracture, 23 ℃ | 9.00 | MPa | ISO 37 |
| TD, fracture, 23 ℃ | 9.00 | MPa | ASTM D412 |
| TD, 100% strain, 23 ℃ | 3.90 | MPa | ASTM D412 |
| TD, 100% strain, 23 ℃ | 3.90 | MPa | ISO 37 |
| Tensile strain | |||
| TD, fracture, 23 ℃ | 550 | % | ISO 37 |
| TD, fracture, 23 ℃ | 550 | % | ASTM D412 |
| Compression deformation | ASTM D395B | ||
| 23℃，168 hr | 31 | % | ASTM D395B |
| 70℃，22 hr | 40 | % | ASTM D395B |
| 100℃，168 hr | 55 | % | ASTM D395B |
| Compression deformation | ISO 815 | ||
| 23℃，168 hr | 31 | % | ISO 815 |
| 70℃，22 hr | 40 | % | ISO 815 |
| 100℃，168 hr | 55 | % | ISO 815 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 15 seconds, 23 ℃ | 86 | ISO 868 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Relative temperature index | |||
| Electrical performance | 90.0 | ℃ | UL 746 |
| Strength mechanical performance | UL 746 | ||
| 1.5 mm | 85.0 | ℃ | UL 746 |
| 3.0 mm | 90.0 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | |||
| 23 ℃，2 mm | 28 | kV/mm | ASTM D149 |
| Compared to the leakage tracing index | PLC 0 | UL 746 | |
| High Arc Burning Index (HAI) | PLC 0 | UL 746 | |
| High voltage arc ignition resistance index (HVAR) (PLC) | PLC 6 | UL 746 | |
| High voltage arc marking rate | |||
| HVTR | PLC 2 | UL 746 | |
| Hot wire ignition | |||
| HWI | PLC 3 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.50 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 | UL 94 | |
| Extreme oxygen index | 27 | % | ASTM D2863 |
| Extreme oxygen index | 27 | % | ISO 4589-2 |
| Process Conditions | |||
|---|---|---|---|
| Nominal value | Unit | Test method | |
| Nominal value | Unit | Test method | |
| 82 | °C | ||
| 3.0 | hr | ||
| 0.080 | % | ||
| 20 | % | ||
| 10 to 52 | °C | ||
| Fast | |||
| 0.345 to 0.689 | MPa | ||
| 100 to 200 | rpm | ||
| 4.1 to 6.9 | kN/cm² | ||
| 3.18 to 6.35 | mm | ||
| 16.0:1.0 to 20.0:1.0 | |||
| 2.0:1.0 to 2.5:1.0 | |||
| 0.025 | mm | ||
| 82 | °C | ||
| 3.0 | hr | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type 1 |
| 3. Type A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |