Santoprene™ 291-75B150

About
A colorable, specialty thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. It is especially formulated to bond to PC, ABS, PC/ABS, ASA and PMMA for applications where hard/soft combinations are required. This grade of Santoprene TPV is shear-dependent and can be processed on conventional thermoplastics equipment for injection molding or extrusion. It is recyclable within the manufacturing stream.&&

About

A colorable, specialty thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. It is especially formulated to bond to PC, ABS, PC/ABS, ASA and PMMA for applications where hard/soft combinations are required. This grade of Santoprene TPV is shear-dependent and can be processed on conventional thermoplastics equipment for injection molding or extrusion. It is recyclable within the manufacturing stream.&&

Product Description
Supplier	Celanese
Material Status	Commercial: Active
Features	noise reduction,HB,Renewable resources,Agglomerability,Solvent resistance,Ozone resistance,Grease resistance
Availabilitys	Europe,Africa & Middle East ,Asia Pacific,Latin America,North America
Process Methods	Injection Molding,Multiple injection molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.10	g/cm³	ASTM D792
Density	1.10	g/cm³	ISO 1183

elastic body	Nominal value	Unit	Test method
tensile strength
TD, fracture, 23 ℃	15.4	MPa	ASTM D412
TD, fracture, 23 ℃	15.4	MPa	ISO 37
TD, 100% strain, 23 ℃	3.20	MPa	ISO 37
TD, 100% strain, 23 ℃	3.20	MPa	ASTM D412
Tensile strain
TD, fracture, 23 ℃	640	%	ISO 37
TD, fracture, 23 ℃	640	%	ASTM D412
tear strength
TD，23℃	46.0	kN/m	ASTM D624
TD，23℃	46	kN/m	ISO 34-1
Compression deformation			ASTM D395B
23℃，22 hr	37	%	ASTM D395B
70℃，22 hr	68	%	ASTM D395B
Compression deformation			ISO 815
23℃，22 hr	37	%	ISO 815
70℃，22 hr	68	%	ISO 815

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shore A, 15 seconds, 23 ℃	74		ISO 868

Aging performance	Nominal value	Unit	Test method
The rate of change in tensile strength in air (100 ℃, 168 hr)	-8.0	%	ASTM D573
The rate of change in tensile strength in air (100 ℃, 168 hr)	-8.0	%	ISO 188
The rate of change in ultimate elongation in air
100℃，168 hr	-11	%	ASTM D573
Change in Tensile Strain at Break in Air（100℃，168 hr）	-11	%	ISO 188
The rate of change in tensile strength			ASTM D471
23℃，24 hr，in IRM 903 Oil	-4.0	%	ASTM D471
23℃，168 hr，in Cascade Detergent	-16	%	ASTM D471
23℃，168 hr，in Clorox，10%	-16	%	ASTM D471
23℃，168 hr，in Ethanol，50%	-71	%	ASTM D471
23℃，168 hr，in Hydrochloric Acid，10%	-19	%	ASTM D471
23 ℃, 168 hr, at relative humidity of 90%	-9.0	%	ASTM D471
23℃，168 hr，in Sodium Chloride，15%	-18	%	ASTM D471
23℃，168 hr，in Sodium Hydroxide，50%	-16	%	ASTM D471
38 ℃, 168 hr, at relative humidity of 90%	-17	%	ASTM D471
The rate of change in tensile strength			ISO 1817
23℃，24 hr，in IRM 903 Oil	-4.0	%	ISO 1817
23℃，168 hr，in Cascade Detergent	-16	%	ISO 1817
23℃，168 hr，in Clorox，10%	-16	%	ISO 1817
23℃，168 hr，in Ethanol，50%	-71	%	ISO 1817
23℃，168 hr，in Hydrochloric Acid，10%	-19	%	ISO 1817
23 ℃, 168 hr, at relative humidity of 90%	-9.0	%	ISO 1817
23℃，168 hr，in Sodium Chloride，15%	-18	%	ISO 1817
23℃，168 hr，in Sodium Hydroxide，50%	-16	%	ISO 1817
38 ℃, 168 hr, at relative humidity of 90%	-17	%	ISO 1817
Change rate of ultimate elongation			ASTM D471
23℃，24 hr，in IRM 903 Oil	1.0 -4.0	%	ASTM D471
23℃，168 hr，in Cascade Detergent	3.0	%	ASTM D471
23℃，168 hr，in Clorox，10%	-1.0	%	ASTM D471
23℃，168 hr，in Ethanol，50%	-40	%	ASTM D471
23℃，168 hr，in Hydrochloric Acid，10%	-1.0	%	ASTM D471
23 ℃, 168 hr, at relative humidity of 90%	-7.0	%	ASTM D471
23℃，168 hr，in Sodium Chloride，15%	-2.0	%	ASTM D471
23℃，168 hr，in Sodium Hydroxide，50%	2.0	%	ASTM D471
38 ℃, 168 hr, at relative humidity of 90%	-2.0	%	ASTM D471
Changes in tensile stress during fracture			ISO 1817
23℃，24 hr，in IRM 903 Oil	1.0 -4.0	%	ISO 1817
23℃，168 hr，in Cascade Detergent	3.0	%	ISO 1817
23℃，168 hr，in Clorox，10%	-1.0	%	ISO 1817
23℃，168 hr，in Ethanol，50%	-40	%	ISO 1817
23℃，168 hr，in Hydrochloric Acid，10%	-1.0	%	ISO 1817
23 ℃, 168 hr, at relative humidity of 90%	-7.0	%	ISO 1817
23℃，168 hr，in Sodium Chloride，15%	-2.0	%	ISO 1817
23℃，168 hr，in Sodium Hydroxide，50%	2.0	%	ISO 1817
38 ℃, 168 hr, at relative humidity of 90%	-2.0	%	ISO 1817
Change in Durometer Hardness (23 ℃, 168 hr, in Deionized Water)	-2.0		ASTM D471
The rate of change in Shore hardness
Shore A, 23 ℃, 168 hr, in deionized water	-2.0		ISO 1817
Quality change rate			ASTM D471
23℃，168 hr，in Cascade Detergent	0.50	%	ASTM D471
23℃，168 hr，in Clorox，10%	0.50	%	ASTM D471
23℃，168 hr，in Ethanol，50%	8.6	%	ASTM D471
23℃，168 hr，in Hydrochloric Acid，10%	0.50	%	ASTM D471
23 ℃, 168 hr, at relative humidity of 95%	0.10	%	ASTM D471
23℃，168 hr，in Sodium Chloride，15%	0.50	%	ASTM D471
23℃，168 hr，in Sodium Hydroxide，50%	0.10	%	ASTM D471
38 ℃, 168 hr, at relative humidity of 95%	0.50	%	ASTM D471
Quality change rate			ISO 1817
23.0 ℃, 168 hours, at relative humidity of 95%	0.10	%	ISO 1817
23.0℃，168 hr，in Sodium Hydroxide，50%	0.10	%	ISO 1817
30.0 ℃, 168 hours, at relative humidity of 95%	0.50	%	ISO 1817
23.0℃，168 hr，in Cascade Detergent	0.50	%	ISO 1817
23.0℃，168 hr，in Sodium Chloride，15%	0.50	%	ISO 1817
23.0℃，168 hr，in Hydrochloric Acid，10%	0.50	%	ISO 1817
23.0℃，168 hr，in Clorox，10%	0.50	%	ISO 1817
23.0℃，168 hr，in Ethanol，50%	8.6	%	ISO 1817
Volume change			ASTM D471
23℃，168 hr，in Cascade Detergent	0.60	%	ASTM D471
23℃，168 hr，in Clorox，10%	0.60	%	ASTM D471
23℃，168 hr，in Ethanol，50%	9.3	%	ASTM D471
23℃，168 hr，in Hydrochloric Acid，10%	0.60	%	ASTM D471
23 ℃, 168 hr, at relative humidity of 95%	0.10	%	ASTM D471
23℃，168 hr，in Sodium Chloride，15%	0.60	%	ASTM D471
23℃，168 hr，in Sodium Hydroxide，50%	0.20	%	ASTM D471
38 ℃, 168 hr, at relative humidity of 95%	0.60	%	ASTM D471
Volume change			ISO 1817
23℃，168 hr，in Cascade Detergent	0.60	%	ISO 1817
23℃，168 hr，in Clorox，10%	0.60	%	ISO 1817
23℃，168 hr，in Ethanol，50%	9.3	%	ISO 1817
23℃，168 hr，in Hydrochloric Acid，10%	0.60	%	ISO 1817
23 ℃, 168 hr, at relative humidity of 95%	0.10	%	ISO 1817
23℃，168 hr，in Sodium Chloride，15%	0.60	%	ISO 1817
23℃，168 hr，in Sodium Hydroxide，50%	0.20	%	ISO 1817
38 ℃, 168 hr, at relative humidity of 95%	0.60	%	ISO 1817

FLAME CHARACTERISTICS	Nominal value	Test method
Flame retardant level		UL 94
1.60 mm	HB	UL 94
2.10 mm	HB	UL 94

Notes
1. Typical properties: these are not to be construed as specifications.
2. Die C
3. Method Bb, Angle (Nicked)
4. Type 1
5. Type A
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.