| About |
|---|
| A soft, colorable, non-hygroscopic thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material combines good physical properties and chemical resistance for use in a wide range of applications. This grade of Santoprene TPV is shear-dependent and can be processed on conventional thermoplastics equipment for injection molding, extrusion or blow molding. It is polyolefin based and recyclable within the manufacturing stream.&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Material Status | Commercial: Active |
| Features | Low coefficient of friction,Low or no water absorption,Good melt strength,Good coloring,Renewable resources,Solvent resistance,Good Dimensional Stability,Ozone resistance,Clean,HB |
| Availabilitys | Africa & Middle East ,Latin America,Asia Pacific,Europe,North America |
| Process Methods | Extrusion,Multiple injection molding,Profile extrusion,Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.948 | g/cm³ | ASTM D792 |
| Density | 0.950 | g/cm³ | ISO 1183 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| TD, fracture, 23 ℃ | 5.90 | MPa | ASTM D412 |
| TD, fracture, 23 ℃ | 5.90 | MPa | ISO 37 |
| TD, 100% strain, 23 ℃ | 2.20 | MPa | ISO 37 |
| TD, 100% strain, 23 ℃ | 2.20 | MPa | ASTM D412 |
| Tensile strain | |||
| TD, fracture, 23 ℃ | 520 | % | ASTM D412 |
| TD, fracture, 23 ℃ | 520 | % | ISO 37 |
| tear strength | |||
| TD，23℃ | 32 | kN/m | ISO 34-1 |
| TD，23℃ | 32.0 | kN/m | ASTM D624 |
| Compression deformation | |||
| 70℃，22 hr | 29 | % | ASTM D395B |
| 70℃，22 hr | 29 | % | ISO 815 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 15 seconds, 23 ℃ | 64 | ISO 868 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | -60.0 | ℃ | ASTM D746 |
| Embrittlement temperature | -60.0 | ℃ | ISO 812 |
| Relative temperature index | |||
| Electrical performance | 100 | ℃ | UL 746 |
| Strength mechanical performance | UL 746 | ||
| 1.1 mm | 90.0 | ℃ | UL 746 |
| 1.6 mm | 90.0 | ℃ | UL 746 |
| 3.0 mm | 95.0 | ℃ | UL 746 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| The rate of change in tensile strength in air | |||
| 150℃，168 hr | -9.0 | % | ASTM D573 |
| 150℃，168 hr | -9.0 | % | ISO 188 |
| The rate of change in ultimate elongation in air | |||
| 150℃，168 hr | -7.0 | % | ASTM D573 |
| Change in Tensile Strain at Break in Air（150℃，168 hr） | -7.0 | % | ISO 188 |
| Change in Durometer Hardness in Air (150 ℃, 168 hr) | 1.0 | ASTM D573 | |
| The rate of change of Shore hardness in air | |||
| Shaw A, 150 ℃, 168 hr | 1.0 | ISO 188 | |
| Change in Mass in Air（150℃，168 hr） | -8.0 | % | ASTM D573 |
| Change in Mass in Air（150℃，168 hr） | -8.0 | % | ISO 188 |
| The rate of change in tensile strength | ASTM D471 | ||
| 23℃，168 hr，in IRM 903 Oil | -17 | % | ASTM D471 |
| 23℃，168 hr，in Sodium Chloride，15% | -4.0 | % | ASTM D471 |
| 23℃，168 hr，in Sodium Hydroxide，50% | -2.0 | % | ASTM D471 |
| 23℃，168 hr，in Sulfuric Acid，98% | 3.0 | % | ASTM D471 |
| 23 ℃, 168 hr, in water | -3.0 | % | ASTM D471 |
| The rate of change in tensile strength | ISO 1817 | ||
| 23℃，168 hr，in IRM 903 Oil | -17 | % | ISO 1817 |
| 23℃，168 hr，in Sodium Chloride，15% | -4.0 | % | ISO 1817 |
| 23℃，168 hr，in Sodium Hydroxide，50% | -2.0 | % | ISO 1817 |
| 23℃，168 hr，in Sulfuric Acid，98% | 3.0 | % | ISO 1817 |
| 23 ℃, 168 hr, in water | -3.0 | % | ISO 1817 |
| Change rate of ultimate elongation | ASTM D471 | ||
| 23℃，168 hr，in IRM 903 Oil | -21 | % | ASTM D471 |
| 23℃，168 hr，in Sodium Chloride，15% | -5.0 | % | ASTM D471 |
| 23℃，168 hr，in Sodium Hydroxide，50% | -2.0 | % | ASTM D471 |
| 23℃，168 hr，in Sulfuric Acid，98% | 5.0 | % | ASTM D471 |
| 23 ℃, 168 hr, in water | 11 | % | ASTM D471 |
| Changes in tensile stress during fracture | ISO 1817 | ||
| 23℃，168 hr，in IRM 903 Oil | -21 | % | ISO 1817 |
| 23℃，168 hr，in Sodium Chloride，15% | -5.0 | % | ISO 1817 |
| 23℃，168 hr，in Sodium Hydroxide，50% | -2.0 | % | ISO 1817 |
| 23℃，168 hr，in Sulfuric Acid，98% | 5.0 | % | ISO 1817 |
| 23 ℃, 168 hr, in water | 11 | % | ISO 1817 |
| The rate of change in Shore hardness | ASTM D471 | ||
| Shaw A, 23 ℃, 168 hr, in IRM 903 oil | -13 | ASTM D471 | |
| Shore A, 23 ℃, 168 hr, in sodium chloride, 15% | 2.0 | ASTM D471 | |
| Shore A, 23 ℃, 168 hr, in sodium hydroxide, 50% | 2.0 | ASTM D471 | |
| Shore A, 23 ℃, 168 hr, in sulfuric acid, 98% | -1.0 | ASTM D471 | |
| Shaw A, 23 ℃, 168 hr, in water | 0.0 | ASTM D471 | |
| The rate of change in Shore hardness | ISO 1817 | ||
| Shaw A, 23 ℃, 168 hr, in IRM 903 oil | -13 | ISO 1817 | |
| Shore A, 23 ℃, 168 hr, in sodium chloride, 15% | 2.0 | ISO 1817 | |
| Shore A, 23 ℃, 168 hr, in sodium hydroxide, 50% | 2.0 | ISO 1817 | |
| Shore A, 23 ℃, 168 hr, in sulfuric acid, 98% | -1.0 | ISO 1817 | |
| Shaw A, 23 ℃, 168 hr, in water | 0.0 | ISO 1817 | |
| Quality change rate | ASTM D471 | ||
| 23℃，168 hr，in IRM 903 Oil | 47 | % | ASTM D471 |
| 23℃，168 hr，in Sodium Chloride，15% | 0.0 | % | ASTM D471 |
| 23℃，168 hr，in Sodium Hydroxide，50% | 0.0 | % | ASTM D471 |
| 23℃，168 hr，in Sulfuric Acid，98% | 0.0 | % | ASTM D471 |
| 23 ℃, 168 hr, in water | 0.0 | % | ASTM D471 |
| Quality change rate | ISO 1817 | ||
| 23.0℃，168 hr，in Sodium Hydroxide，50% | 0.0 | % | ISO 1817 |
| 23.0℃，168 hr，in Sulfuric Acid，98% | 0.0 | % | ISO 1817 |
| 23.0℃，168 hr，in Sodium Chloride，15% | 0.0 | % | ISO 1817 |
| 23.0℃，168 hr，in IRM 903 Oil | 47 | % | ISO 1817 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | PLC 0 | UL 746 | |
| High Arc Burning Index (HAI) | PLC 0 | UL 746 | |
| High voltage arc ignition resistance index (HVAR) (PLC) | PLC 5 | UL 746 | |
| Hot wire ignition | |||
| HWI | UL 746 | ||
| 1.6 mm | PLC 3 | UL 746 | |
| 3.0 mm | PLC 2 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | UL 94 | ||
| 1.10 mm | HB | UL 94 | |
| 1.60 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Recommended maximum moisture content | 0.080 | % | |
| Proposed maximum recycled material ratio | 20 | % | |
| Barrel rear temperature | 177 to 191 | °C | |
| Barrel middle temperature | 179 to 193 | °C | |
| Barrel front temperature | 185 to 199 | °C | |
| Nozzle temperature | 185 to 210 | °C | |
| Processing (melt) temperature | 143 to 216 | °C | |
| Mold temperature | 24 to 52 | °C | |
| Injection speed | Fast | ||
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 100 to 200 | rpm | |
| Clamping force | 4.1 to 6.9 | kN/cm² | |
| Cushion | 3.18 to 6.35 | mm | |
| Screw length to diameter ratio | 16.0:1.0 to 20.0:1.0 | ||
| Screw compression ratio | 2.0:1.0 to 2.5:1.0 | ||
| Vent depth | 0.025 | mm | |
| Melt temperature | 179 to 216 | °C | |
| Nozzle temperature | 177 to 216 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die C |
| 3. Method Bb, Angle (Nicked) |
| 4. Type 1 |
| 5. Type A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |