| A hard, colorable, specialty, non-hygroscopic thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. It is designed for use in medical and healthcare applications. This grade of Santoprene TPV is shear-dependent and can be processed on conventional thermoplastics equipment for injection molding or blow molding. It is polyolefin based and recyclable within the manufacturing stream.&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Material Status | Commercial: Active |
| Features | Low extract,Low or no water absorption,Biocompatible,Solvent resistance,Radiation disinfection,Ozone resistance,High pressure heat resistance,Good coloring,Renewable resources,Steam sterilized |
| Availabilitys | Asia Pacific,Africa & Middle East ,North America,Latin America,Europe |
| Process Methods | Injection Molding,Multiple injection molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.928 | g/cm³ | ASTM D792 |
| Density | 0.930 | g/cm³ | ISO 1183 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| TD, fracture, 23 ℃ | 13.0 | MPa | ISO 37 |
| TD, fracture, 23 ℃ | 13.0 | MPa | ASTM D412 |
| TD, 100% strain, 23 ℃ | 6.70 | MPa | ISO 37 |
| TD, 100% strain, 23 ℃ | 6.70 | MPa | ASTM D412 |
| Tensile strain | |||
| TD, fracture, 23 ℃ | 650 | % | ISO 37 |
| TD, fracture, 23 ℃ | 650 | % | ASTM D412 |
| tear strength | ASTM D624 | ||
| TD，23℃ | 47.0 | kN/m | ASTM D624 |
| TD，100℃ | 27.0 | kN/m | ASTM D624 |
| tear strength | ISO 34-1 | ||
| TD，23℃ | 47 | kN/m | ISO 34-1 |
| TD，100℃ | 27 | kN/m | ISO 34-1 |
| Compression deformation | |||
| 23℃，168 hr | 36 | % | ASTM D395B |
| 23℃，168 hr | 36 | % | ISO 815 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 15 seconds, 23 ℃ | 94 | ISO 868 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Recommended maximum moisture content | 0.080 | % | |
| Proposed maximum recycled material ratio | 20 | % | |
| Barrel rear temperature | 177 to 191 | °C | |
| Barrel middle temperature | 179 to 193 | °C | |
| Barrel front temperature | 185 to 199 | °C | |
| Nozzle temperature | 185 to 210 | °C | |
| Processing (melt) temperature | 143 to 216 | °C | |
| Mold temperature | 24 to 52 | °C | |
| Injection speed | Fast | ||
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 100 to 200 | rpm | |
| Clamping force | 4.1 to 6.9 | kN/cm² | |
| Cushion | 3.18 to 6.35 | mm | |
| Screw length to diameter ratio | 16.0:1.0 to 20.0:1.0 | ||
| Screw compression ratio | 2.0:1.0 to 2.5:1.0 | ||
| Vent depth | 0.025 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die C |
| 3. Method Bb, Angle (Nicked) |
| 4. Type 1 |
| 5. Type A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |