| About |
|---|
| Sarlink ME-1345N is a general purpose thermoplastic elastomer used in automotive applications, including exterior. Sarlink ME-1345N is a medium hardness, low density, lubricated grade that can be processed by injection molding and extrusion.&& |
| Product Description | |
|---|---|
| Supplier | Teknor Apex |
| Generic | TPE |
| Material Status | Commercial: Active |
| Features | Low liquidity,Smoothness,Lubricating,Low density |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| tensile strength | ISO 37 | ||
| fracture | 5.80 | MPa | ISO 37 |
| MD, fracture | 1.90 | MPa | ISO 37 |
| TD, 100% strain | 0.73 | MPa | ISO 37 |
| MD, 100% strain | 1.36 | MPa | ISO 37 |
| Tensile strain | ISO 37 | ||
| fracture | 820 | % | ISO 37 |
| Flow rate, fracture | 350 | % | ISO 37 |
| tear strength | ISO 34-1 | ||
| TD | 12 | kN/m | ISO 34-1 |
| MD | 18 | kN/m | ISO 34-1 |
| Compression deformation | ISO 815 | ||
| 22℃，70 hr | 27 | % | ISO 815 |
| 23℃，22 hr | 12 | % | ISO 815 |
| 90℃，70 hr | 47 | % | ISO 815 |
| 125℃，70 hr | 68 | % | ISO 815 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ISO 868 | ||
| Shore A, 1 second, injection molding | 47 | ISO 868 | |
| Shore A, 5 seconds, injection molding | 45 | ISO 868 | |
| Shore A, 15 seconds, injection molding | 43 | ISO 868 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| The rate of change in tensile strength in air | ISO 188 | ||
| TD：110℃，1008 hr | 43 | % | ISO 188 |
| MD：110℃，1008 hr | 5.3 | % | ISO 188 |
| TD: 100% strain at 110 ℃, 1008 hr | 5.5 | % | ISO 188 |
| MD: 100% strain at 110 ℃, 1008 hr | 6.6 | % | ISO 188 |
| TD：125℃，168 hr | 69 | % | ISO 188 |
| MD：125℃，168 hr | 11 | % | ISO 188 |
| TD: 100% strain 125 ℃, 168 hr | 21 | % | ISO 188 |
| MD: 100% strain 125 ℃, 168 hr | 13 | % | ISO 188 |
| Changes in tensile stress during fracture in air | ISO 188 | ||
| TD：110℃，1008 hr | 5.5 | % | ISO 188 |
| Flow rate: 125 ℃, 168 hr | 15 6.8 | % | ISO 188 |
| TD：125℃，1008 hr | 6.1 | % | ISO 188 |
| The rate of change of Shore hardness in air | ISO 188 | ||
| Shore A, 110 ℃, 1008 hr | 3.8 | ISO 188 | |
| Shore A, 110 ℃, 1008 hr | 3.2 | ISO 188 | |
| Shore A, 110 ℃, 1008 hr | 3.9 | ISO 188 | |
| Shaw A, 125 ℃, 168 hr | 1.6 | ISO 188 | |
| Shaw A, 125 ℃, 168 hr | 2.5 | ISO 188 | |
| Shaw A, 125 ℃, 168 hr | 2.7 | ISO 188 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 0.890 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 200℃，5.0kg | 5.0 | g/10min | ASTM D1238 |
| Apparent viscosity of melt | |||
| 200℃，206 sec^-1 | 258 | Pa·s | ASTM D3835 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Barrel rear temperature | 182 to 232 | °C | |
| Barrel middle temperature | 188 to 238 | °C | |
| Barrel front temperature | 193 to 243 | °C | |
| Nozzle temperature | 199 to 249 | °C | |
| Processing (melt) temperature | 199 to 249 | °C | |
| Mold temperature | 35 to 49 | °C | |
| Injection pressure | 1.38 to 5.52 | MPa | |
| Injection speed | Fast | ||
| Back pressure | 0.172 to 0.689 | MPa | |
| Screw speed | 50 to 100 | rpm | |
| Cushion | 3.81 to 25.4 | mm | |
| Barrel 1 zone temperature | 182 to 232 | °C | |
| Barrel 2 zone temperature | 188 to 238 | °C | |
| Barrel 3 zone temperature | 193 to 243 | °C | |
| Barrel 5 zone temperature | 199 to 249 | °C | |
| Nozzle temperature | 199 to 249 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type 1, 20 in/min |
| 3. Method Ba, Angle (Unnicked), 20 in/min |
| 4. Type A |
| 5. Type 1 |
| 6. 5 sec |
| 7. 1 sec |
| 8. 15 sec |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |