| About |
|---|
| Sarlink TPV 24587 is a high performance thermoplastic vulcanizate used in automotive & consumer/industrial applications. Sarlink TPV 24587 is a high hardness, low density, lubricated grade exhibiting excellent tear strength. This grade is suitable for both injection molding and extrusion.&& |
| Product Description | |
|---|---|
| Supplier | Teknor Apex |
| Generic | TPV |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Excellent Processability,Low liquidity,Good Hardness,Lubricating,Low density,Good tear strength,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| elastic body | Nominal value | Unit | Test method |
| tensile strength | ISO 37 | ||
| TD, 100% strain | 5.77 | MPa | ISO 37 |
| MD, 100% strain | 8.43 | MPa | ISO 37 |
| Tensile strain | ISO 37 | ||
| fracture | 470 | % | ISO 37 |
| Flow rate, fracture | 440 | % | ISO 37 |
| tear strength | ISO 34-1 | ||
| TD | 74 | kN/m | ISO 34-1 |
| MD | 45 | kN/m | ISO 34-1 |
| Compression deformation | ISO 815 | ||
| 23℃，22 hr | 32 | % | ISO 815 |
| 70℃，22 hr | 49 | % | ISO 815 |
| 90℃，70 hr | 58 | % | ISO 815 |
| 125℃，70 hr | 76 | % | ISO 815 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ISO 868 | ||
| Shore A, 1 second, injection molding | 90 | ISO 868 | |
| Shore A, 5 seconds, injection molding | 87 | ISO 868 | |
| Shore A, 15 seconds, injection molding | 86 | ISO 868 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Relative temperature index | |||
| Electrical performance | 50.0 | ℃ | UL 746 |
| Strength mechanical performance | 50.0 | ℃ | UL 746 |
| Impact mechanical performance | 50.0 | ℃ | UL 746 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| The rate of change in tensile strength in air | ISO 188 | ||
| TD：110℃，1008 hr | 1.1 | % | ISO 188 |
| MD：110℃，1008 hr | -2.5 | % | ISO 188 |
| TD: 100% strain at 110 ℃, 1008 hr | 12 | % | ISO 188 |
| MD: 100% strain at 110 ℃, 1008 hr | 19 | % | ISO 188 |
| TD：125℃，168 hr | -0.80 | % | ISO 188 |
| MD：125℃，168 hr | 9.1 | % | ISO 188 |
| TD: 100% strain 125 ℃, 168 hr | 13 | % | ISO 188 |
| MD: 100% strain 125 ℃, 168 hr | 33 | % | ISO 188 |
| Changes in tensile stress during fracture in air | ISO 188 | ||
| TD：110℃，1008 hr | -9.6 | % | ISO 188 |
| Flow rate: 110 ℃, 1008 hr | -20 | % | ISO 188 |
| TD：125℃，168 hr | -18 | % | ISO 188 |
| Flow rate: 125 ℃, 168 hr | -32 | % | ISO 188 |
| The rate of change of Shore hardness in air | ISO 188 | ||
| Shore A, 110 ℃, 1008 hr | 0.50 | ISO 188 | |
| Shore A, 110 ℃, 1008 hr | 0.20 | ISO 188 | |
| Shore A, 110 ℃, 1008 hr | 0.10 | ISO 188 | |
| Shaw A, 125 ℃, 168 hr | 0.50 | ISO 188 | |
| Shaw A, 125 ℃, 168 hr | 0.20 | ISO 188 | |
| Shaw A, 125 ℃, 168 hr | 0.10 | ISO 188 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.50 mm, all colors | HB | UL 94 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 3.0 | g/10min | ASTM D1238 |
| Apparent viscosity of melt | |||
| 200℃，206 sec^-1 | 264 | Pa·s | ASTM D3835 |
| Special value | Nominal value | Unit | Test method |
|---|---|---|---|
| fracture | 9.20 | MPa | ISO 37 |
| MD, fracture | 12.1 | MPa | ISO 37 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Barrel rear temperature | 173 to 213 | °C | |
| Barrel middle temperature | 179 to 219 | °C | |
| Barrel front temperature | 184 to 224 | °C | |
| Nozzle temperature | 190 to 230 | °C | |
| Processing (melt) temperature | 190 to 230 | °C | |
| Mold temperature | 35 to 60 | °C | |
| Injection pressure | 1.38 to 6.89 | MPa | |
| Injection speed | Fast | ||
| Back pressure | 0.172 to 0.862 | MPa | |
| Screw speed | 50 to 120 | rpm | |
| Cushion | 3.81 to 25.4 | mm | |
| Barrel 1 zone temperature | 166 to 204 | °C | |
| Barrel 2 zone temperature | 171 to 210 | °C | |
| Barrel 3 zone temperature | 177 to 216 | °C | |
| Barrel 4 zone temperature | 179 to 218 | °C | |
| Barrel 5 zone temperature | 182 to 221 | °C | |
| Nozzle temperature | 190 to 227 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type 1, 20 in/min |
| 3. Method Ba, Angle (Unnicked), 20 in/min |
| 4. Type A |
| 5. Type 1 |
| 6. 1 sec |
| 7. 5 sec |
| 8. 15 sec |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |