| About |
|---|
| SARLINK® TPV 3100 series are engineered materials designed primarily for general purpose, automotive and industrial applications requiring a good balance of thermal, mechanical, and physical properties. SARLINK® 3135, available in NAT and BLK, is a low hardness, low density, multi-purpose thermoplastic vulcanizate that can be processed by injection molding, blow molding or extrusion for applications such as grips, seals, gaskets, profiles, hose & tubes, bellows, and other articles.&& |
| Product Description | |
|---|---|
| Supplier | Teknor Apex |
| Generic | TPV |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good flexibility,Good surface appearance,High elastic,High Heat Resistance,Good bond,Elastic,Low density,Low Hardness,Solvent resistance,Higher melt stability,Agglomerability,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.930 | g/cm³ | ASTM D792 |
| Density | 0.930 | g/cm³ | ISO 1183 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| TD, 100% strain | 1.10 | MPa | ASTM D412 |
| TD, 100% strain | 1.10 | MPa | ISO 37 |
| MD, 100% strain | 2.10 | MPa | ASTM D412 |
| MD, 100% strain | 2.10 | MPa | ISO 37 |
| tensile strength | |||
| fracture | 4.00 | MPa | ASTM D412 |
| fracture | 4.00 | MPa | ISO 37 |
| MD, fracture | 2.20 | MPa | ASTM D412 |
| MD, fracture | 2.20 | MPa | ISO 37 |
| Tensile strain | |||
| fracture | 600 | % | ASTM D412 |
| fracture | 600 | % | ISO 37 |
| Flow rate, fracture | 200 | % | ISO 37 |
| Flow rate, fracture | 200 | % | ASTM D412 |
| tear strength | |||
| TD | 15 | kN/m | ASTM D624 |
| TD | 15 | kN/m | ISO 34-1 |
| Compression deformation | |||
| 23℃，22 hr | 15 | % | ASTM D395 |
| 23℃，22 hr | 15 | % | ISO 815 |
| 70℃，22 hr | 30 | % | ASTM D395 |
| 70℃，22 hr | 30 | % | ISO 815 |
| 125℃，70 hr | 52 | % | ASTM D395 |
| 125℃，70 hr | 52 | % | ISO 815 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 5 seconds, extrusion molding | 38 | ASTM D2240 | |
| Shore A, 5 seconds, extrusion molding | 38 | ISO 868 | |
| Shore A, 5 seconds, injection molding | 43 | ASTM D2240 | |
| Shore A, 5 seconds, injection molding | 43 | ISO 868 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Relative temperature index | |||
| Electrical performance | 50.0 | ℃ | UL 746 |
| Strength mechanical performance | 50.0 | ℃ | UL 746 |
| Impact mechanical performance | 50.0 | ℃ | UL 746 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Change rate of tensile strength in air – TD | |||
| 135℃，1000 hr | 0.0 | % | ASTM D573 |
| 135℃，1000 hr | 0.0 | % | ISO 188 |
| 100% strain 135 ℃, 1000 hr | 4.0 | % | ASTM D573 |
| 100% strain 135 ℃, 1000 hr | 4.0 | % | ISO 188 |
| 150℃，168 hr | 4.0 | % | ASTM D573 |
| 150℃，168 hr | 4.0 | % | ISO 188 |
| 100% strain 150 ℃, 168 hr | 11 | % | ASTM D573 |
| 100% strain 150 ℃, 168 hr | 11 | % | ISO 188 |
| Changes in tensile stress when fractured in air – TD | |||
| 135℃，1000 hr | -2.0 | % | ASTM D573 |
| 135℃，1000 hr | -2.0 | % | ISO 188 |
| 150℃，168 hr | 1.0 | % | ISO 188 |
| 150℃，168 hr | 1.0 | % | ASTM D573 |
| The rate of change of Shore hardness in air | |||
| Shaw A, 135 ℃, 1000 hr | -1.0 | ASTM D573 | |
| Shaw A, 135 ℃, 1000 hr | -1.0 | ISO 188 | |
| Shaw A, 150 ℃, 168 hr | 1.0 | ISO 188 | |
| Shaw A, 150 ℃, 168 hr | 1.0 | ASTM D573 | |
| Volume change | |||
| 125℃，70 hr，in IRM 903 Oil | 150 | % | ASTM D471 |
| 125℃，70 hr，in IRM 903 Oil | 150 | % | ISO 1817 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.50 mm, all colors | HB | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Apparent viscosity of melt – Capillary, @ 206/s | |||
| 200℃ | 270 | Pa·s | ASTM D3835 |
| 200℃ | 270 | Pa·s | ISO 11443 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 82 | °C | |
| Drying time | 3.0 | hr | |
| Barrel rear temperature | 177 to 216 | °C | |
| Barrel middle temperature | 177 to 216 | °C | |
| Barrel front temperature | 177 to 216 | °C | |
| Nozzle temperature | 188 to 221 | °C | |
| Processing (melt) temperature | 182 to 221 | °C | |
| Mold temperature | 10 to 66 | °C | |
| Back pressure | 0.0689 to 0.345 | MPa | |
| Screw speed | 100 to 200 | rpm | |
| Screw length to diameter ratio | 20.0:1.0 | ||
| Drying temperature | 82 | °C | |
| Drying time | 3.0 | hr | |
| Barrel 1 zone temperature | 182 to 204 | °C | |
| Barrel 2 zone temperature | 182 to 204 | °C | |
| Barrel 3 zone temperature | 188 to 210 | °C | |
| Barrel 4 zone temperature | 188 to 210 | °C | |
| Melt temperature | 193 to 216 | °C | |
| Nozzle temperature | 193 to 216 | °C | |
| Traction roller | 21 to 49 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method Ba, Angle (Unnicked) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |