| Sarlink TPV 5165N is a general purpose thermoplastic vulcanizate used in automotive and industrial applications. Sarlink TPV 5165N is a low hardness, medium density grade exhibiting superior compression set and chemical resistance. This grade can be processed by injection molding, extrusion, and profile extrusion. |
| Product Description | |
|---|---|
| Supplier | Teknor Apex |
| Generic | TPV |
| Material Status | Commercial: Active |
| Features | Low Hardness |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Shore hardness | |||
| Shore A, 5 seconds, extrusion molding | 64 | ||
| Shore A, 5 seconds, injection molding | 67 | ||
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| TD, yield | 6.52 | MPa | ASTM D412 |
| TD, 100% strain | 2.60 | MPa | ASTM D412 |
| Tensile strain | |||
| TD, fracture | 650 | % | ASTM D412 |
| tear strength | |||
| TD | 35.0 | kN/m | ASTM D624 |
| Compression deformation | |||
| 70℃，22 hr | 29 | % | |
| 100℃，22 hr | 40 | % |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Change rate of tensile strength in air – TD | |||
| 150℃，168 hr | -7.3 | % | |
| 100% strain, 150 ℃, 168 hr | 3.0 | % | |
| The rate of change in ultimate elongation in air | |||
| TD，150℃，168 hr | -12 | % | ASTM D573 |
| The rate of change in hardness of a hardness tester in the air | |||
| 150℃，168 hr | 1.0 | ASTM D573 |
| Legal Statement | Nominal value | Unit | Test method |
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 0.948 | g/cm³ | ASTM D792 |
| Apparent viscosity of melt | |||
| 200℃，206 sec^-1 | 350 | Pa·s | ASTM D3835 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Squeeze description | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 82 | °C | |
| Drying time | 3.0 | hr | |
| Barrel rear temperature | 177 to 216 | °C | |
| Barrel middle temperature | 177 to 216 | °C | |
| Barrel front temperature | 177 to 216 | °C | |
| Nozzle temperature | 188 to 221 | °C | |
| Processing (melt) temperature | 182 to 221 | °C | |
| Mold temperature | 10 to 66 | °C | |
| Back pressure | 0.0689 to 1.03 | MPa | |
| Screw speed | 100 to 200 | rpm | |
| Screw length to diameter ratio | 20.0:1.0 | ||
| Drying temperature | 82 | °C | |
| Drying time | 3.0 | hr | |
| Barrel 1 zone temperature | 182 to 204 | °C | |
| Barrel 2 zone temperature | 182 to 204 | °C | |
| Barrel 3 zone temperature | 188 to 210 | °C | |
| Barrel 4 zone temperature | 188 to 210 | °C | |
| Melt temperature | 193 to 216 | °C | |
| Nozzle temperature | 193 to 216 | °C | |
| Traction roller | 21 to 49 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |