| Sarlink TPV X10075B is a high performance thermoplastic vulcanizate used in automotive applications. Sarlink TPV X10075B is a medium hardness, low density, RoHS compliant grade suitable for injection molding.&& |
| Product Description | |
|---|---|
| Supplier | Teknor Apex |
| Generic | TPV |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good Dimensional Stability,High Heat Resistance,Solvent resistance |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| elastic body | Nominal value | Unit | Test method |
| tensile strength | ISO 37 | ||
| TD, fracture | 6.10 | MPa | ISO 37 |
| MD, fracture | 5.40 | MPa | ISO 37 |
| Tensile strain | ISO 37 | ||
| TD, fracture | 490 | % | ISO 37 |
| Flow rate, fracture | 410 | % | ISO 37 |
| tear strength | |||
| TD | 30 | kN/m | ISO 34-1 |
| Compression deformation | ISO 815 | ||
| 23℃，22 hr | 24 | % | ISO 815 |
| 70℃，22 hr | 34 | % | ISO 815 |
| 125℃，70 hr | 50 | % | ISO 815 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Change rate of tensile strength in air – TD | ISO 188 | ||
| 135℃，1008 hr | -15 | % | ISO 188 |
| 100% strain 135 ℃, 1008 hr | 5.0 | % | ISO 188 |
| 150℃，168 hr | -25 | % | ISO 188 |
| 100% strain 150 ℃, 168 hr | 0.0 | % | ISO 188 |
| Changes in tensile stress when fractured in air – TD | ISO 188 | ||
| 135℃，1008 hr | -20 | % | ISO 188 |
| The rate of change of Shore hardness in air | ISO 188 | ||
| Shaw A, 135 ℃, 1008 hr | 0.0 | ISO 188 | |
| Shaw A, 150 ℃, 168 hr | -3.0 | ISO 188 | |
| Volume change | |||
| 125 ℃, 70 hr, in IRM 903 oil | 70 | % | ISO 1817 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ISO 868 | ||
| Shore A, 5 seconds, extrusion molding | 73 | ISO 868 | |
| Shore A, 5 seconds, injection molding | 75 | ISO 868 | |
| friction coefficient | 0.40 to 0.50 | ASTM D1894 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 0.936 | g/cm³ | ISO 1183 |
| Apparent viscosity of melt | |||
| 200℃，206 sec^-1 | 190 | Pa·s | ASTM D3835 |
| Special value | Nominal value | Unit | Test method |
|---|---|---|---|
| TD, 100% strain | 2.80 | MPa | ISO 37 |
| MD, 100% strain | 3.50 | MPa | ISO 37 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Barrel rear temperature | 180 to 205 | °C | |
| Barrel middle temperature | 180 to 205 | °C | |
| Barrel front temperature | 180 to 205 | °C | |
| Nozzle temperature | 185 to 210 | °C | |
| Processing (melt) temperature | 185 to 210 | °C | |
| Mold temperature | 10 to 55 | °C | |
| Back pressure | 0.100 to 1.00 | MPa | |
| Screw speed | 100 to 200 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method Ba, Angle (Unnicked) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |