| About |
|---|
| Features Hexene copolymer Outstanding mechanical properties Excellent drawdown Good heat sealing range Good stiffness Applications General packaging thin film (10µm to 30µm) Not recommended for lamination film Blending into LDPE&& |
| Product Description | |
|---|---|
| Supplier | Sasol |
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good heat sealing,Smoothness,Good dissection,High anti-blocking,Food contact compliance,Inoxidizability,Copolymer,Hexene copolymers |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.929 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.0 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | ASTM D1894 | ||
| Self dynamic, blow molded film | 0.12 | ASTM D1894 | |
| Compared to itself – static, blow molded film | 0.12 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 30 | µm | |
| tensile strength | ASTM D882 | ||
| MD, yield, 30 µ m, blow molded film | 12.0 | MPa | ASTM D882 |
| TD, yield, 30 µ m, blow molded film | 12.0 | MPa | ASTM D882 |
| MD : Break, 1.2 mil, Blown Film | 33.0 | MPa | ASTM D882 |
| TD, fracture, 30 µ m, blow molded film | 23.0 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, yield, 30 µ m, blow molded film | 500 | % | ASTM D882 |
| TD, yield, 30 µ m, blow molded film | 580 | % | ASTM D882 |
| Drop hammer impact | |||
| 30 µ m, blow molded film | 150 | g | ASTM D1709 |
| Elmandorf tear strength | ASTM D1922 | ||
| MD: 30 µ m, blow molded film | 8.0 | g | ASTM D1922 |
| TD: 30 µ m, blow molded film | 27 | g | ASTM D1922 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45° | 45 | ASTM D2457 | |
| Haze | 15 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel temperature | 180 to 190 | °C | |
| Barrel 1 zone temperature | 190 to 200 | °C | |
| Barrel 2 zone temperature | 190 to 200 | °C | |
| Barrel 3 zone temperature | 190 to 200 | °C | |
| Barrel 4 zone temperature | 190 to 200 | °C | |
| Melt temperature | 190 | °C | |
| Nozzle temperature | 190 to 200 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. F50 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |