| Features Medium flow Recommended for use in applications where superior impact properties and toughness are required Excellent balance between impact and stiffness properties Excellent impact toughness properties at low temperatures (-30°C) Contains a nucleating agent which ensures rapid crystallisation, resulting in an improved impact to stiffness balance as well as shorter cooling times Applications Injection moulding Bottle crates Dairy and industrial crates Transport and storage containers Buckets Folding boxes Tool cases Garden tools&& |
| Product Description | |
|---|---|
| Supplier | Sasol |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good flexibility,High impact resistance,Nucleation,Food contact compliance,Moderate liquidity,Low temperature toughness,Antistatic property,low-temperature impact resistance,Impact copolymer |
| Availabilitys | Africa & Middle East ,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.904 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 8.5 | g/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 1.3 | % | ISO 294-4 |
| MD | 1.4 | % | ISO 294-4 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20℃ | 6.5 | kJ/m² | ISO 179/1eA |
| 0℃ | 10 | kJ/m² | ISO 179/1eA |
| 23℃ | 50 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 48.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 80.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| — | 144 | ℃ | ISO 306/A120 |
| B120 | 58.0 | ℃ | ISO 306/B120 |
| Melting temperature | 163 | ℃ | ISO 11357-3 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1050 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| yield | 21.0 | MPa | ISO 527-2/1A/50 |
| Tensile strain | |||
| fracture | > 50 | % | ISO 527-2/1A/50 |
| yield | 6.0 | % | ISO 527-2/1A/50 |
| Bending modulus | 1000 | MPa | ISO 178 |
| Ball hardness | 45.0 | MPa | ISO 2039-1 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Hopper temperature | 40 to 60 | °C | |
| Barrel rear temperature | 180 to 260 | °C | |
| Barrel middle temperature | 220 to 280 | °C | |
| Barrel front temperature | 240 to 280 | °C | |
| Nozzle temperature | 220 to 280 | °C | |
| Processing (melt) temperature | 220 to 280 | °C | |
| Mold temperature | 20 to 60 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. HB |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |