Sasol Polymers PP HRV100

About
Features High flow Narrow molecular weight distribution Suitable for injection moulded products where rigidity and shorter cycle times are required Offers easy extrusion processability when used for producing: Staple fibre in the range 4-40 denier per filament on short spin integrated lines Continuous filament (CF) production on multi position spin / draw / wind or short spin / warp / wind processes Applications Injection moulding Household and domestic articles Caps and closures Cosmetic and toiletry components Extrusion Narrow weave strapping Sewing yarns&&

About

Features High flow Narrow molecular weight distribution Suitable for injection moulded products where rigidity and shorter cycle times are required Offers easy extrusion processability when used for producing: Staple fibre in the range 4-40 denier per filament on short spin integrated lines Continuous filament (CF) production on multi position spin / draw / wind or short spin / warp / wind processes Applications Injection moulding Household and domestic articles Caps and closures Cosmetic and toiletry components Extrusion Narrow weave strapping Sewing yarns&&

Product Description
Supplier	Sasol
Generic	PP homopolymerization
Material Status	Commercial: Active
Features	Excellent Processability,High liquidity,Quick molding cycle,Food contact compliance,Weight distribution,Homopolymer
Availabilitys	Africa & Middle East ,Asia Pacific,Europe
Process Methods	Extrusion

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.905	g/cm³	ISO 1183
Melt Flow Rate
230℃，2.16kg	22	g/10min	ISO 1133
Shrinkage rate			ISO 294-4
TD	1.3	%	ISO 294-4
MD	1.3	%	ISO 294-4

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength
23℃	2.5	kJ/m²	ISO 179/1eA

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	52.0	℃	ISO 75-2/A
0.45 MPa, unannealed	83.0	℃	ISO 75-2/B
Vicat Softening Temp
—	152	℃	ISO 306/A120
B120	88.0	℃	ISO 306/B120
Melting temperature	163	℃	ISO 11357-3

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	1400	MPa	ISO 527-2/1A/1
tensile strength
yield	33.0	MPa	ISO 527-2/1A/50
Tensile strain
fracture	> 50	%	ISO 527-2/1A/50
yield	9.0	%	ISO 527-2/1A/50
Bending modulus	1350	MPa	ISO 178
Ball hardness	70.0	MPa	ISO 2039-1

Process Conditions
injection	Nominal value	Unit	Test method
Extrusion	Nominal value	Unit	Test method
Hopper temperature	40 to 60	°C
Barrel rear temperature	180 to 260	°C
Barrel middle temperature	220 to 280	°C
Barrel front temperature	240 to 280	°C
Nozzle temperature	220 to 280	°C
Processing (melt) temperature	220 to 280	°C
Mold temperature	20 to 60	°C
Hopper temperature	40 to 60	°C
Barrel 1 zone temperature	200 to 280	°C
Barrel 2 zone temperature	240 to 280	°C
Barrel 3 zone temperature	240 to 280	°C
Barrel 4 zone temperature	240 to 280	°C
Barrel 5 zone temperature	220 to 280	°C
Melt temperature	220 to 280	°C
Nozzle temperature	220 to 240	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.