| About |
|---|
| Features Very high flow Narrow molecular weight distribution Suitable for the injection moulding of thin walled articles with high flow path / wall thickness ratios Contains a nucleating agent which ensures rapid crystallisation, resulting in an improved impact to stiffness balance as well as shorter cooling times Suitable for use in extrusion coating processes where the grade offers melt curtain stability and less necking Applications Injection moulding Food containers Caps and closures Pharmaceutical containers Thin walled packaging Extrusion Extrusion coating of woven PP cloth&& |
| Product Description | |
|---|---|
| Supplier | Sasol |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | High liquidity,Nucleation,Good stripping performance,Food contact compliance,Weight distribution,Homopolymer |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 50 | g/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 1.2 | % | ISO 294-4 |
| MD | 1.2 | % | ISO 294-4 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 2.5 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 55.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 90.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | |||
| — | 155 | ℃ | ISO 306/A120 |
| B120 | 92.0 | ℃ | ISO 306/B120 |
| Melting temperature | 163 | ℃ | ISO 11357-3 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1650 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| yield | 35.0 | MPa | ISO 527-2/1A/50 |
| Tensile strain | |||
| fracture | > 50 | % | ISO 527-2/1A/50 |
| yield | 8.5 | % | ISO 527-2/1A/50 |
| Bending modulus | 1600 | MPa | ISO 178 |
| Ball hardness | 75.0 | MPa | ISO 2039-1 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Hopper temperature | 40 to 60 | °C | |
| Barrel rear temperature | 180 to 260 | °C | |
| Barrel middle temperature | 220 to 280 | °C | |
| Barrel front temperature | 240 to 280 | °C | |
| Nozzle temperature | 220 to 280 | °C | |
| Processing (melt) temperature | 220 to 280 | °C | |
| Mold temperature | 20 to 60 | °C | |
| Hopper temperature | 40 to 60 | °C | |
| Barrel 1 zone temperature | 220 to 300 | °C | |
| Barrel 2 zone temperature | 260 to 300 | °C | |
| Barrel 3 zone temperature | 260 to 300 | °C | |
| Barrel 4 zone temperature | 260 to 300 | °C | |
| Barrel 5 zone temperature | 260 to 300 | °C | |
| Melt temperature | 240 to 300 | °C | |
| Nozzle temperature | 260 to 300 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. HB |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |