| About |
|---|
| SCANAMID 6 B/C12^ F30 is a Polyamide 66/6 Copolymer (Nylon 66/6) product filled with 30% glass fiber. It is available in Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated.&& |
| Product Description | |
|---|---|
| Supplier | Polykemi |
| Generic | PA66/6 |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.36 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 1.0 | % | ISO 294-4 |
| MD | 0.30 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 160 | MPa | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 8500 | MPa | ISO 178 |
| bending strength | 225 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 10 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 210 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 200 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | > 195 | ℃ | ISO 306 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 | |
| Igniting temperature of the hot wire | |||
| 2 mm | 650 | ℃ | IEC 60695-2-13 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 120°C/h |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |