| About |
|---|
| 15% glass fibre reinforced PA-PP-blend with excellent chemical resistance and low dependence of humidity |
| Product Description | |
|---|---|
| Supplier | A. Schulman |
| Generic | PA+PP |
| Material Status | Commercial: Active |
| Features | Solvent resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.12 | g/cm³ | ISO 1183/A |
| Melt Volume Rate | |||
| 250℃，2.16 kg | 10.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| TD | 1.2 | % | |
| MD | 0.50 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 5200 | MPa | ISO 527-2/1A/1 |
| Tensile stress | |||
| fracture | 90.0 | MPa | ISO 527-2/1A/5 |
| Tensile strain | |||
| fracture | 3.5 | % | ISO 527-2/1A/5 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 14 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 40 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 183 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed | 150 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| A50 | 210 | ℃ | ISO 306 |
| B50 | 151 | ℃ | ISO 306 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | > 1.0E+15 | ohms·cm | IEC 62631-3-1 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning rate | |||
| 2.0 mm | < 100 | mm/min | ISO 3795 |
| 2.0 mm | < 100 | mm/min | FMVSS 302 |
| Flammability level | |||
| 1.5 mm | HB | ||
| 3.0 mm | HB |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 80 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Processing (melt) temperature | 240 to 270 | °C | |
| Mold temperature | 60 to 90 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |