| About |
|---|
| Impact modified Copolyester compound with high scratch- and chemical resistance, high transparence for brillant surfaces&& |
| Product Description | |
|---|---|
| Supplier | A. Schulman |
| Generic | PCTG |
| Material Status | Commercial: Active |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.17 | g/cm³ | ISO 1183/A |
| Melt Volume Rate | |||
| 265℃，2.16 kg | 10.0 | cm³/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 8.0 | kJ/m² | |
| 23℃ | 70 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 无断裂 | ||
| 23℃ | 无断裂 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 100 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed | 85.0 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| A50 | 115 | ℃ | ISO 306/A50 |
| B50 | 110 | ℃ | ISO 306 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | |||
| 1.6 mm | HB | ||
| 3.2 mm | HB |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H358/30 | 84.0 | MPa | ISO 2039-1 |
| Tensile modulus | 1600 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| yield | 50.0 | MPa | |
| fracture | 45.0 | MPa | |
| Tensile strain | |||
| yield | 6.0 | % | ISO 527-2/1A/50 |
| Nominal tensile fracture strain | 80 | % | ISO 527-2/1A/50 |
| Bending modulus | |||
| 23℃ | 1750 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 70.0 | MPa | |
| 3.50% strain, 23 ℃ | 54.0 | MPa |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90 | °C | |
| Drying time | 4.0 | hr | |
| Recommended maximum moisture content | 5.0E-3 to 0.015 | % | |
| Proposed maximum recycled material ratio | 20 | % | |
| Processing (melt) temperature | 280 to 300 | °C | |
| Mold temperature | 60 to 80 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |