| About |
|---|
| 30% glass fibre reinforced PBT/ASA-blend with high surface quality and reduced warpage&& |
| Product Description | |
|---|---|
| Supplier | A. Schulman |
| Generic | PBT+ASA |
| Material Status | Commercial: Active |
| Features | Low warping,Good surface appearance,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.43 | g/cm³ | ISO 1183/A |
| Melt Volume Rate | |||
| 250℃，2.16 kg | 18.0 | cm³/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 10000 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| fracture | 125 | MPa | ISO 527-2/1A/5 |
| Tensile strain | |||
| fracture | 2.0 | % | ISO 527-2/1A/5 |
| Bending modulus | 8500 | MPa | ISO 178 |
| bending strength | 172 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 7.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 35 | kJ/m² | ISO 179/1eU |
| 23℃ | 40 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 186 | ℃ | ISO 75-2/Af |
| 0.45 MPa, unannealed | 213 | ℃ | ISO 75-2/Bf |
| Vicat Softening Temp | |||
| A50 | 202 | ℃ | ISO 306/A50 |
| B50 | 133 | ℃ | ISO 306 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | 200 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | IEC 60695-11-10, -20 | ||
| 1.5 mm | HB | IEC 60695-11-10, -20 | |
| 3.0 mm | HB | IEC 60695-11-10, -20 | |
| Glowing wire flammability index | IEC 60695-2-12 | ||
| 1.5 mm | 700 | ℃ | IEC 60695-2-12 |
| 3.0 mm | 750 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 1.5 mm | 725 | ℃ | IEC 60695-2-13 |
| 3 mm | 775 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 20 | % | ISO 4589-2 |
| Flame retardant level | 30 | mm/min | FMVSS 302 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.050 | % | |
| Proposed maximum recycled material ratio | 20 | % | |
| Processing (melt) temperature | 250 to 260 | °C | |
| Mold temperature | 60 to 90 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |