| 50% glass fiber reinforced PA 6, high strength and stiffness, heat stabilized&& |
| Product Description | |
|---|---|
| Supplier | A. Schulman |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.55 | g/cm³ | |
| Shrinkage rate | |||
| TD | 0.70 | % | |
| MD | 0.20 | % | |
| Viscosity number | 145 | cm³/g | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 10 | kJ/m² | |
| 23℃ | 15 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 90 | kJ/m² | |
| 23℃ | 95 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 215 | ℃ | |
| 1.8 MPa, unannealed | 205 | ℃ | |
| Vicat Softening Temp | |||
| — | 216 | ℃ | |
| — | 212 | ℃ | |
| Ball pressure test | |||
| 190℃ | 通过 | ||
| 0.75 mm | 125 | ℃ | |
| 1.5 mm | 125 | ℃ | |
| 0.75 mm | 115 | ℃ | |
| 1.5 mm | 120 | ℃ | |
| 3.0 mm | 125 | ℃ | |
| Relative temperature index | |||
| Electrical performance | |||
| Impact mechanical performance | |||
| 0.75 mm | 130 | ℃ | |
| 1.50 mm | 130 | ℃ | |
| 3.00 mm | 140 | ℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning rate | |||
| 2.0 mm | < 100 | mm/min | |
| Flammability level | |||
| 0.75 mm | HB | ||
| 1.5 mm | HB | ||
| 3.0 mm | HB | ||
| Glowing wire flammability index | |||
| 1.5 mm | 650 | ℃ | |
| 3.0 mm | 650 | ℃ |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H358/30 | 280 | MPa | |
| Tensile modulus | 16000 | MPa | |
| tensile strength | |||
| fracture | 210 | MPa | |
| Tensile strain | |||
| fracture | 2.2 | % | |
| Bending modulus | 15000 | MPa | |
| bending strength | 310 | MPa | |
| Bending strain | 3.1 | % |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.040 to 0.10 | % | |
| Proposed maximum recycled material ratio | 20 | % | |
| Processing (melt) temperature | 250 to 280 | °C | |
| Mold temperature | 60 to 100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |