| About |
|---|
| SCHULAMID® 6 MV 14 FR 4 K1681 (Dry) Medium viscosity flame-retardant Polyamide 6 grade (V-2); without PBDE&&SCHULAMID® 6 MV 14 FR 4 K1681 Nylon Unfilled PBDE-Free, GWIT&& |
| Product Description | |
|---|---|
| Supplier | A. Schulman |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Flame Characteristics,V-2 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.26 | g/cm³ | ISO 1183/A |
| Viscosity number | 145 | cm³/g | ISO 307 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 3.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 48 | kJ/m² | ISO 179/1eU |
| 23℃ | 49 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 76.0 | ℃ | ISO 75-2/Af |
| 0.45 MPa, unannealed | 186 | ℃ | ISO 75-2/Bf |
| Vicat Softening Temp | |||
| A50 | 217 | ℃ | ISO 306/A50 |
| B50 | 202 | ℃ | ISO 306 |
| Ball pressure test | |||
| 200℃ | Pass | IEC 60695-10-2 | |
| Flame retardant grade (0.38 mm) | 130 | ℃ | UL 746 |
| 0.75 mm | 130 | ℃ | UL 746 |
| 1.5 mm | 130 | ℃ | UL 746 |
| 3.0 mm | 130 | ℃ | UL 746 |
| Relative temperature index | |||
| Electrical performance | UL 746 | ||
| Strength mechanical performance | UL 746 | ||
| Impact mechanical performance | UL 746 | ||
| Flame retardant grade (0.38 mm) | 75.0 | ℃ | UL 746 |
| 0.75 mm | 90.0 | ℃ | UL 746 |
| 1.5 mm | 100 | ℃ | UL 746 |
| 3.0 mm | 100 | ℃ | UL 746 |
| Flame retardant grade (0.38 mm) | 100 | ℃ | UL 746 |
| 0.75 mm | 110 | ℃ | UL 746 |
| 1.5 mm | 120 | ℃ | UL 746 |
| 3.0 mm | 120 | ℃ | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | 300 | V | IEC 60112 |
| High Arc Burning Index (HAI) | UL 746 | ||
| Flame retardant grade (0.38 mm) | PLC 0 | UL 746 | |
| 0.75 mm | PLC 0 | UL 746 | |
| 1.5 mm | PLC 0 | UL 746 | |
| 3.0 mm | PLC 0 | UL 746 | |
| Hot wire ignition | |||
| HWI | UL 746 | ||
| Flame retardant grade (0.38 mm) | PLC 4 | UL 746 | |
| 0.75 mm | PLC 4 | UL 746 | |
| 1.5 mm | PLC 2 | UL 746 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning rate | ISO 3795 | ||
| 0.380 mm, Self-Extinguishing | 0.0 | mm/min | ISO 3795 |
| 0.75 mm, automatic fire extinguishing | 0.0 | mm/min | ISO 3795 |
| 1.5mm, automatic fire extinguishing | 0.0 | mm/min | ISO 3795 |
| 3.0 mm, automatic fire extinguishing | 0.0 | mm/min | ISO 3795 |
| Flame retardant level | UL 94 | ||
| 0.38 mm | V-2 | UL 94 | |
| 0.75 mm | V-2 | UL 94 | |
| 1.50 mm | V-2 | UL 94 | |
| 3.00 mm | V-2 | UL 94 | |
| Flammability level | IEC 60695-11-10, -20 | ||
| Flame retardant grade (0.38 mm) | V-2 | IEC 60695-11-10, -20 | |
| 0.75 mm | V-2 | IEC 60695-11-10, -20 | |
| 1.5 mm | V-2 | IEC 60695-11-10, -20 | |
| 3.0 mm | V-2 | IEC 60695-11-10, -20 | |
| Glowing wire flammability index | IEC 60695-2-12 | ||
| 0.38 mm | 850 | ℃ | IEC 60695-2-12 |
| 0.75 mm | 850 | ℃ | IEC 60695-2-12 |
| 1.5 mm | 960 | ℃ | IEC 60695-2-12 |
| 3.0 mm | 960 | ℃ | IEC 60695-2-12 |
| Igniting temperature of the hot wire | IEC 60695-2-13 | ||
| 0.38 mm | 825 | ℃ | IEC 60695-2-13 |
| 0.75 mm | 825 | ℃ | IEC 60695-2-13 |
| 1.5 mm | 825 | ℃ | IEC 60695-2-13 |
| 3 mm | 825 | ℃ | IEC 60695-2-13 |
| Extreme oxygen index | 23 | % | ISO 4589-2 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3800 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| yield | 70.0 | MPa | ISO 527-2/1A/50 |
| Tensile strain | |||
| yield | 3.0 | % | ISO 527-2/1A/50 |
| Ball hardness | |||
| H358/30 | 160 | MPa | ISO 2039-1 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | < 0.10 | % | |
| Proposed maximum recycled material ratio | 25 | % | |
| Processing (melt) temperature | 240 to 270 | °C | |
| Mold temperature | 50 to 80 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Dry as molded |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |