| About |
|---|
| Schularene™ N3103 is a high heat PLA. This material achieves a higher heat deflection temperature as standard PLA. The heat performance is similar to PS, PP and ABS. As powder it’s used for laminating adhesive in textile or automotive applications. We recommend for most applications pre-drying before processing.&& |
| Product Description | |
|---|---|
| Generic | PLA |
| Material Status | Commercial: Active |
| Features | Renewable resources,High Heat Resistance,Good bond |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.24 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 210℃，2.16kg | 30 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 3000 | MPa | ASTM D638 |
| tensile strength | 45.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 5.0 | % | ISO 527-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 5.0 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 105 | ℃ | ISO 75-2/B |
| Melting peak temperature | 190 to 220 | ℃ | DSC |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |